Abstract:The oxide layer formed by ultra‐high melt point oxides (ZrO2, HfO2) and SiO2 glassy melt is the key to the application of traditional thermal structural materials in extremely high‐temperature environment. However, the negative effect of ZrO2 and HfO2 phase transitions on the stability of oxide layer and rapid volatilization of low viscosity SiO2 melt limit its application in aerospace. In this study, the ablation behavior of Cf/(CrZrHfNbTa)C‒SiC high‐entropy composite was explored systematically via an air plasma ablation test, under a heat flux of 5 MW/m2 at temperatures up to 2450°C. The composite presents an outstanding ablation resistance, with linear and mass ablation rates of 0.9 μm/s and 1.82 mg/s, respectively. This impressive ablation resistance is attributed to the highly stable oxide protective layer formed in situ on the ablation surface, which comprises a solid skeleton of (Zr, Hf)6(Nb, Ta)2O17 combined with spherical particles and SiO2 glassy melt. The irregular particles provide a solid skeleton in the oxides protective layer, which increased stability of the oxide layer. Moreover, the spherical particles have a crystal structure similar to that of Ta2O5 and are uniformly distributed in SiO2 glassy melt, which hinder the flow of SiO2 glassy melt and enhance its viscosity to a certain degree. And it reduces the volatilization of SiO2. In summary, the stable oxide layer was formed by irregular particles oxide and the SiO2 glassy melt with certain viscosity, thereby resulting in the impressive ablation resistance of the composite. This study fills a gap in ablation research on the (CrZrHfNbTa)C system.

Investigation of anti-ablation property of Cf/HfC composite prepared at 1900°C by reactive melt infiltration

Microstructure and ablation behavior of C/C–HfC–SiC composites fabricated by reactive melt infiltration with Hf–Si alloy

Ablation behavior and mechanisms of Cf/(CrZrHfNbTa)C‒SiC high‐entropy composite at temperatures up to 2450°C

Ablation behavior and mechanisms of 3D-Cf/Ta0.8Hf0.2C-SiC composite at temperatures up to 2500 °C

Ablation mechanism of Cf/(Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C-SiC composite during plasma ablation above 2000 °C

Ablation behavior of HfC coating with different thickness for carbon/carbon composites at ultra-high temperature

Ablation behavior and mechanisms of Cf/(Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C–SiC high-entropy ceramic matrix composites

Ablation behavior of C/C–Zr1-xHfxC-SiC composites under an oxyacetylene flame at above 2500 °C

Ablation-resistant Ta0.78Hf0.22C solid solution ceramic modified C/C composites for oxidizing environments over 2200 °C

Cyclic ablation behavior of mullite-modified C/C-HfC-SiC composites under an oxyacetylene flame at about 2400 °C

Ablation behavior of high-entropy boride (Hf-Zr-Ta-Ti)B 2 coating fabricated via supersonic atmospheric plasma spraying for carbon/carbon composites

Ablation behaviors and mechanisms of Cf/HfCPIP-SiCCVI composites: From SiO2 nanowires film to HfO2 skeleton

Ultra-high temperature ablation behavior of CVD-Hf 5 TaC 6 solid solution ceramic coating for C/C composites: Experiment and first-principle calculation

Ablation mechanism and morphology evolution of the HfC-SiC coating for C/C composites deposited by supersonic atmospheric plasma spraying

Investigation on the oxidation and ablation behaviors of HfB2-SiC-Si/SiC-Si coatings for carbon/carbon composites

Ablation behavior of 3D PyC-Cf/SiHfBOC Composites under an oxyacetylene torch environment above 2000 °C

Influences of deposition temperature, gas flow rate and ZrC content on the microstructure and anti-ablation performance of CVD-HfC-ZrC coating

Comparative ablation behaviors of C/SiC–ZrC and C/SiC–HfC composites prepared by ceramization of carbon aerogel preforms

Microstructure and Ablation Behavior of C/C-SiC-(ZrxHf1−x)C Composites Prepared by Reactive Melt Infiltration Method

Fabrication of low-density carbon-bonded carbon fiber composites with an Hf-based coating for high temperature applications

Effect of HfC addition on ablation behavior of SiBCN ceramics