Abstract:Wide-potential supercapacitor systems are highly anticipated to put aside the low-energy roadblock caused by the finite electrolysis voltage (1.23 V). However, poor electrolyte kinetics within the popular activated carbon electrodes usually downgrades the inherent high-power supply and long-cycle tolerance. To address this issue, multimodal porous carbon nanostructures are fabricated by the spontaneous cross-coupling between tetrachloro-1,4-benzoquinone (network joint) and four aromatic amines (chain motif) with varying bond dissociation energies, followed by temperature-programmed alkali thermolysis. The representative electrode with a broad ion-accessible platform (2539 m(2) g(-1)) stands out by virtue of substantial electrosorption spaces (<1 nm micropores) and multi-level pore highways nested in open macroporous voids, enabling an instant ion-transport kinetics response (0.40 Omega s(-0.5)) and remarkable rate capability (80.4% capacitance retention up to 20 A g(-1)) in the H2SO4 electrolyte. Moreover, a LiOTf/NaOTf hybrid water-in-salt electrolyte is developed here to shift the water-splitting potential, wherein double Li+/Na+ cations can weaken strong Coulombic interactions for low migration barrier and dense interface accumulation. Consequently, the upgraded symmetric device using such concentrated aqueous medium, displays a boosted energy capacity of 39.2 Wh kg(-1)@550 W kg(-1), an extraordinary power response of 22 kW kg(-1) under high-energy delivery up to 28.2 Wh kg(-1), and a durable service lifespan (85.5% energy retention over 10 000 successive cycles). This inspiring work provides structural insights for designing carbon electrodes adaptive to safe, wide-potential but kinetically sluggish electrolytes, realizing comprehensive energy-power improvements in supercapacitors.

Fluorine Modification over Activated Carbon Electrodes Enabling Stable 3 V Supercapacitor Operation

Boosting Supercapacitive Performance of Flexible Carbon Via Surface Engineering.

Preparation and Electrochemical Properties of PF-based Activated Carbon

Vaporized Hydrothermal Functionalization of Carbon Fiber and Its Superior Supercapacitor Performance

Fluorine-rich Nanoporous Carbon with Enhanced Surface Affinity in Organic Electrolyte for High-Performance Supercapacitors

A high-performance supercapacitor based on activated carbon fibers with an optimized pore structure and oxygen-containing functional groups

Effect of fluorine functional groups introduced into activated carbon aerogel by carbon tetrafluoride plasmas in supercapacitors

Adapting a Kinetics-Enhanced Carbon Nanostructure to Li/Na Hybrid Water-in-Salt Electrolyte for High-Energy Aqueous Supercapacitors

Great Enhancement of Carbon Energy Storage through Narrow Pores and Hydrogen-Containing Functional Groups for Aqueous Zn-Ion Hybrid Supercapacitor

Reclaimed Carbon Fiber-Based 2.4 V Aqueous Symmetric Supercapacitors

Fluorine and nitrogen co-doped mesoporous carbon derived from polytetrafluoroethylene@melamine sponge for supercapacitor application

Facile Synthesis of Fluorine-Doped Graphene Aerogel with Rich Semi-Ionic C–F Bonds for High-Performance Supercapacitor Application

Facile Synthesis of Fluorine-Doped Hollow Mesoporous Carbon Nanospheres for Supercapacitor Application

Recent advances in fluorine-doped/fluorinated carbon-based materials for supercapacitors

Electrochemical and Hydrothermal Activation of Carbon Fiber Supercapacitor Electrode

Three-Dimensional Functionalized Graphenes with Systematical Control over the Interconnected Pores and Surface Functional Groups for High Energy Performance Supercapacitors

Nanosized Fe 3 O 4 -Modified Activated Carbon for Supercapacitor Electrodes

N-Doped Porous Carbon-Nanofiber-Supported Fe3C/Fe2O3 Nanoparticles as Anode for High-Performance Supercapacitors

Research progress on hydroxide fluoride-based electrode materials for supercapacitors

Activated Carbon Supercapacitor Electrodes Prepared by a Casting Method

Trial Producing the Supercapacitor with Activated Carbon Fiber Electrode