Abstract:In preparing Cu2ZnSnSe4 (CZTSe) thin films, selenization at high Se pressure is likely to form a thick molybdenum diselenide (MoSe2) layer. An excessively thick MoSe2 layer degrades the performance of CZTSe solar cells. Annealing under low Se pressure has been suggested to prevent the formation of such a thick MoSe2 layer. However, the potential loss of Sn metal from CZTSe thin films at low Se pressure or high temperature raises the additional difficulty of controlling the compositions and phases of the films. Carefully controlling these selenization parameters to yield high-quality CZTSe thin films is important. This study investigates the loss of Sn and the formation of molybdenum diselenide in CZTSe thin films at low Se pressure. Three-step selenization at low Se pressure is performed on an electrodeposited Cu/Sn/Zn precursor to prepare high-quality CZTSe thin films. In the first step, rapid thermal annealing with a substrate temperature of 500°C and a low Se vapor pressure of 4.6Pa was performed to reduce the loss of Sn and the thickness of the MoSe2 layer, and thus to obtain a Cu-poor and Zn-rich film. In the second step, a high annealing temperature of 570°C and an inert gas at high pressure was used to improve elemental diffusion and increase the uniformity of the elemental distribution. In the third step, thermal annealing with a substrate temperature of 500°C and a low Se vapor pressure of 4.6Pa was performed to reduce the loss of Sn and the thickness of the MoSe2 layer, and to eliminate the impurity phase of SnSe (which was formed in the second step of annealing) on the surface of the CZTS films. The loss of Sn and the formation of molybdenum diselenide in the CZTSe thin films are negligible when this three-step selenization at low Se pressure is used. When the selenization parameters are properly controlled, CZTSe solar cells with an efficiency of as high as 8.2% can be obtained.

Optimization of the Selenization Pressure Enabling Efficient Cu2ZnSn(S,Se)4 Solar Cells

Optimization of the Selenization Pressure Enabling Efficient Cu 2 ZnSn(S,Se) 4 Solar Cells

Formation of Alloyed Cu2Cox Zn1-x Sn(S,Se)4 Absorption Layer and Its Application in Solar Cells

Segmented Control of Selenization Environment for High‐Quality Cu2ZnSn(S,Se)4 Films Toward Efficient Kesterite Solar Cells

Unveiling the Selenization Reaction Mechanisms in Ambient Air-Processed Highly Efficient Kesterite Solar Cells

A CZTSe Solar Cell with 8.2% Power Conversion Efficiency Fabricated Using Electrodeposited Cu/Sn/Zn Precursor and a Three-Step Selenization Process at Low Se Pressure

Passivation of Deep‐Level Defects through Chemical Environment Regulation for Efficient CZTSSe Solar Cells Based on Active Selenium Adsorption–Desorption Process

Achieving 11.23 % Efficiency in CZTSSe Solar Cells Via Defect Control and Interface Contact Optimization

Toward High Efficient Cu2 ZnSn(Sx ,Se1- x )4 Solar Cells: Break the Limitations of VOC and FF

Positive Role of Inhibiting CZTSSe Decomposition on Intrinsic Defects and Interface Recombination of 12.03% Efficient Kesterite Solar Cells

Toward High Efficient Cu2ZnSn(Sx,Se1−x)4 Solar Cells: Break the Limitations of VOC and FF

Surprising Efficiency Enhancement of Cu2ZnSn(S,Se)4 Solar Cells with Abnormal Zn/Sn Ratios

A precisely regulating phase evolution strategy for highly efficient kesterite solar cells

Surprising Efficiency Enhancement of Cu 2 ZnSn(S,Se) 4 Solar Cells with Abnormal Zn/Sn Ratios

Controlling selenization equilibrium enables high-quality Cu2ZnSn(S, Se)4 absorbers for efficient solar cells

Energy Band Alignment and Defect Synergistic Regulation Enable Air-Solution-Processed Kesterite Solar Cells with the Lowest VOC Deficit.

10.24% Efficiency of Flexible Cu2 ZnSn(S,Se)4 Solar Cells by Pre-Evaporation Selenization Technique

Passivating SnZn Defect and Optimizing Energy Level Alignment via Organic Silicon Salt Incorporation toward Efficient Solution‐Processed CZTSSe Solar Cells

Suppressing Element Inhomogeneity Enables 14.9% Efficiency CZTSSe Solar Cells

Kesterite Cu2znsn(S,Se)(4) Solar Cells with Beyond 8% Efficiency by A Sol Gel and Selenization Process

Defect Control for 12.5% Efficiency Cu2ZnSnSe4 Kesterite Thin-Film Solar Cells by Engineering of Local Chemical Environment