Abstract:Terahertz (THz) non-destructive testing can detect internal defects in dielectric materials. However, this technology is mainly used for detecting thin and simple structures at present, lacking validations for the detection effectiveness of internal defects in thicker and more complex structures, such as fiber-web-reinforced composite sandwich panels. In this study, samples of fiber-web-reinforced polymethacrylimide foam sandwich panels, which are, respectively, 20 mm and 30 mm thick, were made to detect the internal debonding, inclusion, pore, and crack defects by the THz time-domain spectroscopy system (THz-TDS). The peak-to-peak-imaging algorithm, maximum-amplitude-imaging algorithm, minimum-amplitude-imaging algorithm, pulse-width-imaging algorithm, and time-of-flight-imaging algorithm were used to process and image the collected THz signals. The results showed that the peak-to-peak-imaging algorithm had the best performance. To address the low imaging resolution of THz-TDS, a block-based super-resolution reconstruction method—SSSRGAN—is proposed, which can improve image resolution while maintaining the clear edge contours of defects. The defect-detection results of the samples showed that THz-TDS could detect all pore, debonding, and crack defects, with a minimum size of 3 mm for pores and debonding and a minimum thickness of 1 mm for cracks. The method showed poor detection performance for inclusions with a thickness of 0.053 mm, but could still extract the defect features. Based on the THz-TDS reflection mode measurement principle, the thickness information of the panel, foam core, and web of the samples was calculated: the measurement error was no more than 0.870 mm for Sample #1 and no more than 0.270 mm for Sample #2, demonstrating the accuracy of THz-TDS in measuring the dimensions of sandwich panel structures. In general, THz technology shows potential for detecting internal defects and performing dimensional measurements in complex structures. With the advancement of portable devices and enhancements in detection speed, real-time on-site detection is anticipated in the future.

A Study on the Terahertz Nondestructive Testing of Foam Sandwich Structure Composites Based on Morphological Filtering

Research on Internal Defect Detection of Epoxy Glass Fiber Composites Based on Terahertz Imaging Technology

Nondestructive Evaluation of Special Defects Based on Ultrasound Metasurface

Non-Destructive Testing of a Fiber-Web-Reinforced Polymethacrylimide Foam Sandwich Panel with Terahertz Time-Domain Spectroscopy

Ultrasonic Detection Method of Micro Defects in Thick-Section CFRP

Linear frequency modulation infrared thermal imaging detection technology for GFRP/PMI foam sandwich structure defects

Defect detection of GFRP/Nomex honeycomb sandwich structure by linear frequency modulation infrared thermal imaging

Measurement Methodology: Terahertz Technique: A Non-Destructive Testing Method for Composite Defect Detection

Aerogel Defect Detection Using Terahertz Waves

Optimization of Thermal-Wave Radar Thermography by Transverse Heat Flow Suppression Technique for Accurate Defect Detection of CFRP Laminates

Research on pulse infrared thermal wave detection technology for honeycomb sandwich structure defects

LFM-Chirp-Square pulse-compression thermography for debonding defects detection in honeycomb sandwich composites based on THD-processing technique

Floquet wave theory-based time-corrected ultrasonic total focusing method for fiber-reinforced composite laminate

Terahertz time-domain spectroscopy for the inspection of dry fibre preforms

Microwave Nondestructive Detection and Quantitative Evaluation of Kissing Defects in GFRP Laminates

A novel nondestructive testing method for honeycomb structure using acoustic band gap

Terahertz Nondestructive Testing of Honeycomb Composites Based on FMCW Technology

Simulation for Embedded-Defects Foam Terahertz Images of Active Bifocal Terahertz Imaging System at 0.22 THz Based on Geometric Optics

Effects of Diffuse and Specular Reflections on Detecting Embedded Defects of Foams With a Bifocal Active Imaging System at 0.22 THz

Optimized ultrasonic total focusing imaging of diverse and multiple defects in crossply CFRP: Floquet wave theory, numerical simulation, and experimental validation

Infrared defect recognition technology for composite materials