Abstract:The oxidation behavior of a Ni3Al-based superalloy IC6 coated with a duplex Re–Cr–Ni–Mo diffusion barrier layer and an Al reservoir layer was investigated in air at 1423K for up to 1080ks. The diffusion barrier layer was formed by electroplating Re(Ni) and Ni films on the alloy, followed by Cr pack cementation at 1573K, and as a result, forms a continuous inner Re–Cr–Ni–Mo diffusion barrier layer and an outer Ni(Cr,Mo,Al) layer. Then a Ni film was electroplated on the Ni(Cr,Mo,Al) layer, followed by Al-pack cementation at 1273K for 18ks, to form an Al reservoir layer with a duplex Ni2Al3 and γ-Ni(Cr,Mo,Al) layers. After oxidation at 1423K in air for 1080ks, the Al reservoir layer changed to a γ-Ni–4Cr–5Mo–12Al (all in at%) layer, on which a protective α-Al2O3 scale formed. The Re–Cr(Mo)–Ni layer was stable and effectively retarded the interdiffusion between the Al reservoir layer and the alloy, as a result, the depth of the microstructural change zone of the alloy was less than 15μm. In contrast, the bare and the coated IC6 superalloy only with an Al reservoir layer were significantly oxidized, accompanied by serious spallation of oxide scales. After oxidation at 1423K for 1080ks, the depth of the microstructural change zone of the alloy was about 200μm for the bare and coated alloy only with an Al reservoir layer. These results indicate that the oxidation resistance of IC6 superalloy can be effectively improved by coating with a Re–Cr–Ni–Mo diffusion barrier layer and an Al reservoir layer.

Synergistic Effect of Re-base Diffusion Barrier and Pt Modification on the Oxidation Behaviour of NiCrAlY Coatings

Preparation and Oxidation Behavior of NiCrAlY Coatings with Re-base Diffusion Barrier on a Nickel-Based Single-Crystal Superalloy

Effect of Re-base Diffusion Barrier on the Oxidation Performance of a Gradient NiCoCrAlY Coating

High Temperature Performance and Interface Evolution of a NiCoCrAlY Coating with Pt Modification and Re-based Diffusion Barrier

Influences of MCrAlY Coatings and TBCs on Oxidation Behavior of a Ni-Based Single Crystal Superalloy

Preparation and oxidation performance of a low-diffusion Pt-modified aluminide coating with Re-base diffusion barrier

Improving Cyclic Oxidation Resistance of Ni3Al-based Single Crystal Superalloy with Low-Diffusion Platinum-Modified Aluminide Coating

Preparation and Enhanced Isothermal Oxidation Resistance of a Low Diffusivity NiRePtAl Single-Phase Coating

Cyclic oxidation behavior of Pt modified NiCoCrAlYHfZr + AlNiY coating on a Ni-based single crystal superalloy

Interface stability of NiCrAlY coating without and with a Cr or Mo diffusion barrier on Ti-42Al-5Mn alloy

Modification of NiCoCrAlY with Pt: Part I. Effect of Pt Depositing Location and Cyclic Oxidation Performance

Interdiffusion mechanism at the interface between TiAl alloy and NiCoCrAlY bond coating

Oxidation Performance and Interdiffusion Behavior of a Pt-Modified Aluminide Coating with Pre-deposition of Ni

Improvement in oxidation resistance of a Ni3Al-based superalloy IC6 by rhenium-based diffusion barrier coatings

High-temperature Oxidation Behaviour of Refurbished (ni,pt)al Coating on Ni-based Superalloy at 1100 °C

Oxidation Behavior of Graded NiCrAlYRe Coatings at 900, 1000 and 1100 °C

Microstructure evolution and interdiffusion behaviors of (Ni,Pt)Al coating with and without Re-diffusion barrier on IC21 substrate at 1100°C

Microstructure Evolution and Cyclic Oxidation Performance of Cr2AlC As Active Diffusion Barrier for NiCrAlY Coating on TiAl Alloy

A Magnetron Sputtered Microcrystalline Β-Nial Coating for SC Superalloys. Part II. Effects of a NiCrO Diffusion Barrier on Oxidation Behavior at 1100 °C

On the Oxidation and Interdiffusion Behavior of an AlCoCrFeNiY High-Entropy Alloy Bond Coat on a Directionally Solidified Ni-based Superalloy

Influence of Aluminum and Rhenium on the Isothermal Oxidation Behavior of CoNiCrAlY Alloys