Abstract:PtAl and MCrAlY coating were prepared on the fourth generation single crystal superalloy. The isothermal oxidation tests of superalloys with different coatings were performed at 1150 °C and 1200 °C in a muffle furnace with static air for 500 h. The isothermal oxidation behavior and mechanism of two coatings at 1150 °C and 1200 °C was investigated. MCrAlY coating improved oxidation resistance by forming adhesive oxide scales with pegs, and PtAl coating formed dense and coherent oxide scales on surface to hinder the diffusion of oxygen. Compared with two coatings, a smaller oxidize increasing weight of PtAl coating (0.54 mg/cm 2 ) than MCrAlY coating (2.48 mg/cm 2 ) indicated that PtAl coating presented a better oxidation resistance during oxidation test at ultra high temperature, although a significant interdiffusion behavior occurred between PtAl coating and substrate. Besides, the interactive behavior between Ru and coatings was also investigated. Ru in fourth generation single crystal superalloy could diffuse into β-NiAl phase of coatings, maintaining the integrity of coatings. The major difference between MCrAlY coating and PtAl coating came in the amounts of β-NiAl phase, which leading to the difference on the oxidation resistance between MCrAlY and PtAl. The mechanism about influence of temperature on the oxidation property on bare alloy, MCrAlY-DD91 and PtAl-DD91 was also discussed. Ultra high temperature would promote more elements to participate in the reaction with oxygen, change the compositions of oxide scale and phases, resulting to the spallation of oxide scale and decrease of oxidation resistance.

High-temperature Oxidation Behaviour of Refurbished (ni,pt)al Coating on Ni-based Superalloy at 1100 °C

Influences of MCrAlY Coatings and TBCs on Oxidation Behavior of a Ni-Based Single Crystal Superalloy

High temperature oxidation and interdiffusion behavior of recoated NiCoCrAlY coating on a nickel-based superalloy

Oxidation Behavior and Oxide Transformation of a Pt-Modified Aluminide Coating at Moderate High Temperature

High Temperature Performance and Interface Evolution of a NiCoCrAlY Coating with Pt Modification and Re-based Diffusion Barrier

High-temperature Performance of (ni,pt)al Coatings on Second-Generation Ni-base Single-Crystal Superalloy at 1100 °C: Effect of Excess S Impurities

Oxidation Behavior of Graded NiCrAlYRe Coatings at 900, 1000 and 1100 °C

Cyclic oxidation behavior of Pt modified NiCoCrAlYHfZr + AlNiY coating on a Ni-based single crystal superalloy

Pt-modification on the thermal cycling behavior of NiCoCrAlYTa coating: a case study

Investigation on the Oxidation Behavior of the NiCrAlY Bond-Coat with Low Al Content Sprayed by High Velocity Oxygen Fuel Method

Improving Cyclic Oxidation Resistance of Ni3Al-based Single Crystal Superalloy with Low-Diffusion Platinum-Modified Aluminide Coating

Mechanical and Oxidation Resistance of Remanufactured NiCoCrAlYTa Coating Deposited Via Arc Ion Plating

Oxidation Performance and Interdiffusion Behavior of a Pt-Modified Aluminide Coating with Pre-deposition of Ni

Synergistic Effect of Re-base Diffusion Barrier and Pt Modification on the Oxidation Behaviour of NiCrAlY Coatings

Effect of Nickel Aluminide Microcrystalline Coating on High-Temperature Oxidation Behavior of NiAl-33.5%Cr-0.5%Zr Alloy

High-temperature performance of Pt-modified Ni-20Co-28Cr-10Al-0.5Y coating: Formation mechanism of Pt-rich overlayer and its effect on thermally grown oxide failure

High-temperature Corrosion Behaviour of Pt-modified Aluminide Coating with Solid NaCl Deposit in O2 + 10 Vol% H2O and the Influence of Pre-Oxidation Treatment

Effect of coatings on oxidation behavior of a fourth generation Ni-based single crystal superalloys at ultra high temperature

Tensile crack inhibition of a PtReAl coated Ni 3 Al-based single crystal superalloy after long-term oxidation

Tuning the secondary reaction zone between PtAl coating and nickel based single crystal superalloy during high-temperature oxidation through regulating aluminizing time

Effect of Pre-Oxidation on High-Temperature Oxidation Behavior of Al-Si Coating on Nickel-Based Superalloy