Abstract:Cementitious materials composed entirely of solid waste are expected to replace cement and alleviate environmental pollution problems. Due to limitations in reaction rate and strength, a composite activator comprising NaOH and water glass was employed to investigate the effect of composite activator content (0–12.0% Na2O equivalent) on pore solution pH, hydration products, microscopic morphology, and pore structure of ternary alkali-activated materials prepared by blast furnace slag, desulfurization gypsum and carbide slag. Additionally, the microstructure development results were corroborated through characterization of fluidity, setting time and compressive strength. Results indicate that the reaction process of alkali-activated material accelerates as Na2O equivalent increases from 0 to 8.0%, thereby promoting calcium aluminum silicate gel and hydrotalcite formation, and facilitating the continuous filling of pores, which leads to a dense structure formation. However, excessive gel products are generated on bonded particle surface when Na2O equivalent exceeds 8.0%, hindering polymerization process; meanwhile, the presence of microcracks leads to an increase in macropores (≥10 mm3) proportion resulting in a decrease in compressive strength. Notably, the increase in Na2O equivalent gradually suppresses ettringite formation. Life cycle assessment demonstrates that the preparation of mortar is more environmentally sustainable. Based on the optimal compressive strength, the reduction in global warming, abiotic resource depletion, acidification, and eutrophication potential of mortar compared with cement is 78.7%, 39.7%, 17.9% and 29.2%, respectively. This work contributes to further improving the resource utilization of solid waste, and extending the application of conventional solid waste cementitious materials in the domain of emergency repair engineering.

One-Part Alkali Activated Slag Using Ca(Oh)(2) And Na2co3 Instead Of Naoh As Activator: More Excellent Compressive Strength And Microstructure

Preparation of Coal Gasification Coarse Slag-Based Alkaline Activator and Its Activation Mechanism in Alkali-Activated Slag

Understanding the Role of Calcium Silicate Slag in Sodium Carbonate-Activated Green Materials: Influence on Kinetics, Strength, and Efflorescence

Using calcium carbide residue to prepare ecological alkali activated slag composites: Effect of anion type

Microstructures and properties of alkali-activated slags with composite activator: Effects of Na2O equivalents

Calcium Carbide Residue As Auxiliary Activator for One-Part Sodium Carbonate-Activated Slag Cements: Compressive Strength, Phase Assemblage and Environmental Benefits

The Effect of Activators on the Mechanical Properties and Microstructure of Alkali-Activated Nickel Slag

STUDY ON THE ALKALI-ACTIVATED CEMENTITIOUS MATERIALS PREPARED WITH ALKALI SLAG

Study on the Characteristics of Crystal Formation and Transformation of Alkali-Activated Slag Minerals Induced by Weak Alkali

Ultra-fine Slag Activated by Sodium Carbonate at Ambient Temperature

Controlling the Hydration Rate of Alkali-Activated Slag by the Slow Release of NaOH

Alkali Activated Slag Binder: Effect of Cations from Silicate Activators

Effect of combined activator of Ca(OH)<sub>2</sub> and Na2CO<sub>3</sub> on workability and compressive strength of alkali-activated ferronickel slag system

Comparison of Mechanical Properties and Microstructure of GGBS-based Cementitious Materials Activated by Different Combined Alkaline Wastes

Ground Granulated Blast-Furnace Slag/fly Ash Blends Activated by Sodium Carbonate at Ambient Temperature

Properties of Alkali-Activated Slag Cement Activated by Weakly Alkaline Activator

Hydration Properties and Microstructure Characteristics of Alkali–activated Steel Slag

The Effect of Alkaline Activator on Workability and Compressive Strength of Alkali-Activated Slag Concrete

Hydration and Properties of Slag Cement Activated by Alkali and Sulfate

Long Term Mechanical Properties of Alkali Activated Slag

Effects of Different Activators on Autogenous Shrinkage of Alkali-Activated Slag Cement