Effect of Heat Treatment on Corrosion and Mechanical Properties of Mg-10Y-1.5Zn-0.5Zr Alloy
Mingming Liu,Quanan Li,Xiaoya Chen,Xiangyu Li,Peijun Chen,Jinfeng Tan
DOI: https://doi.org/10.1007/s11665-022-07238-w
IF: 2.3
2022-08-23
Journal of Materials Engineering and Performance
Abstract:In this paper, the microstructure evolution, corrosion and mechanical properties of Mg-10 Y-1.5 Zn-0.5 Zr alloy under different heat treatment conditions were studied systematically. The results demonstrate that the microstructure of the as-cast Mg-10Y-1.5Zn-0.5Zr alloy was mainly constituted of the α -Mg matrix, W(Mg 3 Y 2 Zn 3 ), and 18R-LPSO(Mg 12 YZn) phases. After solution treatment, LPSO phase changed from 18R to 14H-LPSO(Mg 12 YZn), and the microstructure of solid solution alloy was mainly constituted of the α -Mg matrix and 14R-LPSO(Mg 12 YZn) phase. After aging treatment, the microstructure was mainly constituted of the α -Mg matrix, W′(Mg 3 Y 2 Zn 3 ), and 14H-LPSO(Mg 12 YZn) phases. The as-cast Mg-10Y-1.5Zn-0.5Zr alloy had the optimal corrosion resistance performance, and the corrosion rate was 7.55 mm∙y −1 . The mechanical properties of the aging Mg-10Y-1.5Zn-0.5Zr alloy was optimal, the ultimate tensile strength, yield strength, and elongation were 248.12 MPa, 164.94 MPa and 11.12%, respectively.
materials science, multidisciplinary