Abstract:The microstructure of the Al1.0Cr1.4Pr1.6Zr (mass%) alloy after homogenized at 500°C for 400h has been investigated. Addition of Cr, Pr and Zr in combination into pure aluminum results in the formation of submicron Zr-containing PrCr2Al20 and nanoscale Cr, Pr-containing Al3Zr dispersed phases. Compared with the Al1.0Cr1.4Pr and Al1.6Zr alloys, a denser distribution of new fine multicomponent dispersed phases and their superimposition effect are associated with enhanced precipitation-hardening behavior of Al1.0Cr1.4Pr1.6Zr alloy. (doi:10.2320/matertrans.M2013149) The alloys with the nominal chemical compositions of Al1.6Zr, Al1.0Cr1.4Pr and Al1.0Cr1.4Pr1.6Zr (all in mass%) were prepared by melting high purity Al (99.9mass%) with AlZr, AlCr and AlPr master alloys using a conventional casting method. The cast ingots were homogenized at 500°C for 400h, and then quenched in water at ambient temperature. The microstructure was observed using an optical microscope. The phase composition was measured by X-ray diffractometry (XRD) in reflection with Cu-Ki radiation. The morphologies and compositions of large intermetallic particles were measured using energy dispersive X-ray spectroscopy (EDS) in a JSM-6360LV scanning electron microscopy (SEM). To investigate the fine precipitates, TEM observation was performed by a TECNAI G 2 20 microscopy and a Jeol JEM-2010F field-emission transmission electron microscopy equipped with a scanning unit. Thin foils for standard TEM observation were prepared by the standard electrolytic twin-jet polishing technique in a7 5% methanol and 25% nitric acid solution cooled down to ³253K with an applied potential of 1215V and current of 7090mA. The Brinell hardness was measured with a HRBVU-187.5 hardness tester at a load of 980N.

Analysis of Precipitation in a Cu-Cr-Zr Alloy

Analysis of phases in a Cu–Cr–Zr alloy

Microstructure and phase components of the as-cast Cu-0.4%Cr-0.12%Zr-0.01%Si

Study on Aging Precipitation in Cu-Cr-Zr-Mg Alloy

Control of precipitates in CuCrZr alloy

Formation of Fine Multicomponent Precipitates and Enhanced Precipitation-Hardening in an Al–Cr–Pr–Zr Alloy

Quantitative Analysis of Precipitation in an Al–Zn–Mg–Cu–Li Alloy

The influence of Zr concentration on the microstructure and properties of Cu-0.6Cr-xZr alloy: High-throughput preparation and characterization study

Precipitation Behavior of Supersaturated Solid-solubility CuCrZr Alloy by Additive Manufacturing

Precipitation Behavior in Al-Zn-Mg-Cu Alloy after Direct Quenching

Research on aging precipitation in a Cu–Cr–Zr–Mg alloy

Microstructure of QCr0.5 and Cu-Cr-Zr Alloys Before and after Heat Treatment

3D-AP and Positron Annihilation Study of Precipitation Behavior in Cu–Cr–Zr Alloy

Precipitation of Zr2Cu Stable Crystalline Phase from Zr70Cu27.5Rh2.5 Amorphous Alloy

Precipitates and Precipitation Behavior in Al–Zr–Yb–Cr Alloys

Effects of Zr addition on the liquid phase separation and the microstructures of Cu-Cr ribbons with 18-22 at.% Cr

Quantitative Evaluation of Precipitates in an Al–Zn–Mg–Cu Alloy after Isothermal Aging

Investigation of Precipitation Phases in As-Cast Wedge Ingot of Bulk Amorphous Zr56.6cu17.3ni12.5al9.6ti4 Alloy

Effect of Zr on Precipitation Kinetics of Fe-Cr-Al Alloys

The Precipitation Behavior and Mechanical Properties of Cast Al-4.5Cu-3.5Zn-0.5Mg Alloy

Precipitation Behaviour of Al3Zr Precipitate in Al–Cu–Zr and Al–Cu–Zr–Ti–V Alloys