Ultrahigh Temperature Ablation Resistant HfB2-SiC Composites: from Liquid SiHfCB Precursor Synthesis to Light Weight Bulk Preparation and Characterization
Yang Lyu,Jianchao Hao,Yuan Cheng,Wuju Wang,Zhihong Han,Guangdong Zhao,Ruichen Ni,Pu Liu,Hangyu Li,Guiqing Chen,Xinghong Zhang,Wenbo Han
DOI: https://doi.org/10.1016/j.jmst.2024.04.080
2025-01-01
Journal of Material Science and Technology
Abstract:The current generation of ultrahigh temperature ceramic precursors typically encounters obstacles in achieving high ceramic yields ( < 40 wt.%) due to the challenges in integrating significant amounts of boron, which hampers their conversion into boride-based ultrahigh temperature ceramics. To tackle these challenges, a serious of pioneering liquid multi-component hafnium-containing ceramic SiHfCB precursors (with different Hf/Si ratios) have been developed. These novel precursors are featured with stable molecular structure and high ceramic yield which were successfully created through a novel one-pot polymerization process. They present in liquid form and their structure is characterized by C-C bonds forming its main chain with branched chains of O-Si-O, Si-O-Hf, Si-O-B, and B-O-Hf which have untapped advantages including uniform component dispersion, and excellent fluidity. The ceramic yield of SiHfCB precursor with Hf/Si of 0.2 is remarkably up to 68.6 wt.% at 1500 degrees C, and their Hf content exceeded 50 wt.%. Of particular interest, the pyrolyzed product HfB2 -SiC nanopowders derived from the SiHfCB precursor with Hf/Si of 0.2, consist of nanopowders in the 40-60 nm range with a density of 5.23 g cm(-4). Remarkably, this material demonstrates exceptional performance in ultrahigh temperature oxygen-containing environments at 2500 degrees C, showing near-zero ablation with a linear ablation rate of just 2.5 x 10(-4) mm s(-1) . Post-ablation analysis of the microstructure reveals that the formation of a lava-like HfO2 and HfO2 -SiO2 oxide layer effectively blocks oxygen penetration and provides excellent oxidation resistance. The innovative SiHfCB hafnium-containing ceramic precursor offers a groundbreaking solution for the preparation of lightweight ultrahigh-temperature ceramics. This development is poised to provide robust technical support for the use of ultrahigh temperature ceramics in non-ablative thermal protective systems, particularly in the construction of hypersonic vehicles, where ultrahigh temperature resilience is crucial. (c) 2024 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.