Abstract:A W/ZrC/SiC multilayer coating was prepared on C/C composites by reactive melt infiltration (RMI) and atmospheric plasma spray (APS). The morphology and microstructure of the coating were characterized by scanning electron microscopy coupled with energy dispersive spectrometry (SEM‐EDS), X‐ray diffraction (XRD), focused ions beam (FIB) and transmission electron microscope (TEM). Microstructure analysis revealed that the gradient coatings exhibit smooth surface morphology, well‐defined interfaces, uniform thickness and highly dense architecture. After 60 s of ablation, the linear ablation rates (LAR) and mass ablation rates (MAR) of the coated composites stand at 2.58×10−3 mm/s and 5.25×10−3 g/s, respectively. In general, the reason for the great ablation resistance of W/ZrC/SiC coated C/C composites was the comprehensive effect of multilayer coating. The outer W coating was used as the first barrier layer to resist most thermal shocks. Then the molten eutectics SiO2‐ZrO2 formed in ZrC/SiC layer at service temperature could fill the pores and acted as a second diffusion barrier for oxygen and heat.This article is protected by copyright. All rights reserved.

Growth Mechanism and Ablation Behavior of CVD-HfC Coating on the Surface of C/C Composites and CVD-SiC Coating

Ablation mechanism and morphology evolution of the HfC-SiC coating for C/C composites deposited by supersonic atmospheric plasma spraying

Influences of deposition temperature, gas flow rate and ZrC content on the microstructure and anti-ablation performance of CVD-HfC-ZrC coating

SiC Nanowires Toughed HfC Ablative Coating for C/C Composites

Ablation behavior of HfC coating with different thickness for carbon/carbon composites at ultra-high temperature

UHTC coating reinforced by HfC nanowires against ablation for C/C composites

Cyclic ablation behavior and microstructure evolution of multi-layer coating on C/C composites under oxyacetylene torch

Self-densification behavior, interfacial bonding and cyclic ablation resistance of HfSi2-ZrSi2 modified SiC/ZrB2-SiC/SiC coating for Cf/SiC composite

Effect of tantalum carbide on the ablation behaviors of hafnium carbide coating for C/C composites under single and cyclic oxyacetylene torch environments

Investigation on the oxidation and ablation behaviors of HfB2-SiC-Si/SiC-Si coatings for carbon/carbon composites

Microstructures and ablation resistance of WSi2/ZrSi2/ZrxHf1-xC/SiC coating based on a pattern strengthening one-step method

Improvement of ablation resistance of CVD-HfC/SiC coating on hemisphere shaped C/C composites by introducing diffusion interface

Effects of HfC/PyC Core-Shell Structure Nanowires on the Microstructure and Mechanical Properties of Hf1-xZrxC Coating

Ablation behaviour of the CVD-(ZrC/SiC)3 alternate coating on C/C composites under oxyacetylene torch with different heat fluxes

Ablation Resistance of ZrC-based Composite Coating with Multi-Layer Structure for Carbon/carbon Composites above 2200 °C

High-quality SiC-HfC coating with interpenetrating structure based on a two-step low temperature molten salt method

Microstructure and ablation performance of HfC/PyC core-shell structure nanowire-reinforced Hf1-xZrxC coating

Anti-ablation Performance of Plasma Sprayed ZrB2/SiC Coatings on C/C Substrates and the Influence of a Chemical Vapor Deposited SiC Interlayer

Mechanical properties and ablation resistance of La2O3-modified HfC-SiC coating for SiC-coated C/C composites

Cyclic ablation resistance at 2300 °C of (Hf0.4Zr0.4Ta0.2)B2-SiC-Si coating for C/SiC composites prepared by SiC-assisted reactive infiltration of silicon

Microstructure and Ablation Behavior of W/ZrC/SiC Coating on C/C Composites Prepared by Reactive Melt Infiltration and Atmospheric Plasma Spraying