Fabrication Of Tbcu7-Type Single Phase Sm-Fe-Zr-Nb Alloys By Melt-Spinning Combined With High-Energy Ball Milling

Liu Kun,Wang Shuhuan,Feng Yunli,Zhao Dingguo,Zhang Yikun
2021-01-01
Rare Metal Materials and Engineering
Abstract:The complete amorphous phase transformation of Sm-Fe-Zr-Nb alloy powders during high-energy ball milling process was investigated. The effects of milling time on the phase transformation and morphology of the Sm-Fe-Zr-Nb alloy powders were analyzed by X-ray diffraction, scanning electron microscopy, and high-resolution transmission electron microscopy. The result shows that complete amorphous microstructure is obtained after milling for about 2.5 h, and alpha-Fe phase (similar to 5 nm) is precipitated from the amorphous matrix when the milling time is over 3 h. The number of short-range ordered structure increases. The uniform Microstructure and the TbCu7-type single phase are obtained by crystallizing the amorphous precursors milled for 2.5 h. The size of equiaxed grain is similar to 30 nm. This kind of micro-regulation plays a key role in improving the magnetic properties after nitriding.
What problem does this paper attempt to address?