Abstract:In this work, the effect of SiC addition on the microstructure, porosity, phase composition, weight gain, and thickness of TGO of the coatings after repeated oxidation at 1300 °C for various time of APS SiC-YSZ TBCs have been investigated. The phase of the as-sprayed coatings is consisted of t'-ZrO 2 , SiC and very little SiO 2 . With the increase of SiC addition, the diffraction peak intensity of SiC and SiO 2 are both increased. SiC and SiO 2 can fill into the pores in YSZ effectively. However, the porosity in the coatings has little changed with the increased of SiC addition. The addition of SiC during repeated oxidation at 1300 °C can limit the development of the m-ZrO 2 phase while causing no ZrO 2 lattice deformation. Increasing the SiC addition can impede the growth of TGO between the bonding layer and the ceramic layer, lowering the thermal weight gain rate of the SiC-YSZ coating. The lowest thermal weight gain rate occurs when the SiC composite concentration is 15 wt%. When the composite content of SiC is increased by 10 wt%, the percentage of O element at the interface between the bonding layer and the ceramic layer decreases by approximately 6.56 wt%. Increasing the SiC concentration will improve the compactness of the interface between the bonding and ceramic layers, and limit grain formation in the bonding layer. However, the SiC composite composition must match the ceramic coating's porosity. When the SiC percentage is too low, the ceramic layer's porosity increases and TGO development accelerates. When the SiC concentration is too high, it agglomerates and connects within the coating, causing the coating to fail off during high temperature service.

The Oxidation Performance and Interfacial Reaction Behavior of YSZ-ZrB2 Incorporated Glass Composite Coating

Activating Continuous Dislocation Pinning Enhanced Toughness of Nanocomposite Coating Through Specially Oriented Semicoherent Heterointerface Lattice Distortion

Effect of the Y2O3 amount on the oxidation behavior of ZrB2-SiC-based coatings for carbon/carbon composites

Microstructure and oxidation behavior of SiOC coatings on C/C composites co-deposited with HMDS and TEOS by using CVD process

Deposition voltages on the phase evolutions, microstructures, and oxidation behaviors of thermal-resistance Glass-MoSi2-SiC coating

ZrB2 particles reinforced glass coating for oxidation protection of carbon/carbon composites

The enhanced structure stability and the reinforcement mechanism of 0.1Al2O3-ZrO2 reinforced MoSi2 composite coating

Effect of Yb2O3 addition on oxidation/ablation behaviors of ZrB2-MoSi2 composite coating under different environment

High temperature oxidation resistance of Y2O3 modified ZrB2-SiC coating for carbon/carbon composites

Preparation of Al 2 O 3 –zro 2 –Y 2 O 3 Composite Coatings by a Modified Sol–Gel Technique for Thermal Barrier Application

Oxidation Protection of Carbon Fiber by Sol-Gel Derived Boron Doped Yttria Stabilized Zirconia Coatings

Oxidation behaviors and mechanisms of Yb2O3-doped silicon coatings fabricated by vacuum plasma spray

Fabrication and oxidation resistance of mullite/yttrium silicate multilayer coatings on C/SiC composites

Enhanced wet-oxidation resistance of Y2O3 modified SiC ceramics by the formation of Y2Si2O7 protective layer

Microstructure and ultra-high temperature isothermal oxidation behaviour of YSZ-particle-modified WSi2 coating

Isothermal oxidation behavior of NiCoCrAlY/ZrO2 composite coating on γ-TiAl alloy

In-situ SiC nanowires reinforced SiC-based multicomponent ceramic coating for protecting SiOC/CF composites

Oxidation properties of tri-layer ytterbium-disilicate/mullite/silicon-carbide environment barrier coatings for Cf/SiC composites

Effect of Lu2O3 addition on the oxidation behavior of SiC-ZrB2 composite coating at 1500 °C: Experimental and theoretical study

Evolution of Microstructure and Radiative Property of Metal Silicide–glass Hybrid Coating for Fibrous ZrO2 Ceramic During High Temperature Oxidizing Atmosphere

Microstructural evolution and high-temperature oxidation behavior of plasma sprayed SiC-YSZ TBCs