Abstract:The evolution of phase composition and mechanical properties and the formation of oxide layers on Fe40–xNiCoCrAlx (x = 5 and 10 at.%) alloys in long-term oxidation at 900 and 1000°C were studied. In the initial cast state, depending on the aluminum content and valence electron concentration, the alloys contain only an fcc solid solution (VEC = 8 e/a) or a mixture of fcc and bcc phases (VEC = = 7.75 e/a). Thin continuous oxide scales containing Cr2O3 and NiCr2O4 spinel formed on the surface of both alloys oxidized at 900°C for 50 h. A further increase in the annealing time to 100 h leads to the formation of aluminum oxide Al2O3 in the scale on the Fe30Ni25Co15Cr20Al10 alloy, having high protective properties. An increase in the oxidation temperature to 1000°C results in partial failure of the protective layer on the alloy with 10 at.% Al. Long-term holding at 900°C (100 h) + 1000°C (50 h) does not change the phase composition of the Fe35Ni25Co15Cr20Al5 alloy matrix, being indicative of its high thermal stability. In the two-phase Fe30Ni25Co15Cr20Al10 alloy, the quantitative ratio of solid solutions sharply changes: the amount of the bcc phase increases from 4 to 54 wt.% and its B2-type ordering is observed. The mechanical characteristics of the starting alloys and those after long-term high-temperature annealing were determined by automated indentation. The hardness (HIT) and elastic modulus (E) of the cast Fe35Ni25Co15Cr20Al5 alloy are equal to 2 and 147 GPa, respectively, and decrease to 1.8 and 106 GPa after a series of long-term annealing operations. The Fe30Ni25Co15Cr20Al10 alloy shows the opposite dependence: HIT increases from 2.5 in the initial state to 3.1 GPa after annealing and E decreases from 152 to 134 GPa. This indicates that the Fe30Ni25Co15Cr20Al10 alloy is promising as a high-temperature oxidation-resistant and creep-resistant material.

Scaling Behavior of Four Co-20Ni-xCr-yAl (x = 8,15 Wt.%; Y = 3,5 Wt.%) Alloys Exposed to 1 Atm O2 at 1000 °C and 1100 °C

Oxidation Mechanism of Three Fe-Al Alloys with and Without Addition of 0.1 At% Yttrium at 800 °C

High Temperature Oxidation Behavior of Co-20Re-25Cr-2Si Alloy at Different Oxygen Pressures

The Effects of Alloying Elements Cr, Al, and Si on Oxidation Behaviors of Ni-Based Superalloys

Oxidation behavior of AlCoCrFeNiSi high-entropy alloys at 1100 °C

Corrosion Behaviour of Ni-based Alloys 230, 617, and 601 in CO2 Gas at 750 and 850°C

Structural State of High-Entropy Fe40–xNiCoCrAlx Alloys in High-Temperature Oxidation

Effect of Nickel Aluminide Microcrystalline Coating on High-Temperature Oxidation Behavior of NiAl-33.5%Cr-0.5%Zr Alloy

Effect of Al content on the oxidation behavior of NiCoCrAlYHf alloys at 1100°C

Effects of aluminised-coating on microstructure and properties of Ni–Co-base superalloys

Oxidation behavior of a nickel-based single crystal superalloy at 1100 °C under different oxygen concentration

Isothermal Oxidation Resistance of As-cast NiAl and NiAl-(Cr, Mo) Eutectic Alloys at 1000°C

Influences of Al content on oxidation behavior of CoNiCrAlYRe alloys

Effect of Cr and W addition on the oxidation behavior of Ni–8%Al alloy at 1000 °C

High-temperature oxidation behavior of laser additively manufactured AlCrCoNiSi-based high-entropy alloys at 1100 °C

Oxidation Behaviour of Sputter-Depositedni–cr–al Micro-Crystalline Coatings

Wrinkling Behavior of Alumina Scales Formed During Isothermal Oxidation of Fe–Al Binary Alloys

Effects of Ni and Cr on the high-temperature oxidation behavior and mechanisms of Co- and CoNi-base superalloys

Structural and High-Temperature Oxidation Performance of Al-Co-Y Co-deposited Coatings on a TiAl-Nb Alloy at Low Temperatures

Effect of Grain Size on Oxidation Behavior of Fe-40ni-15cr Alloys

Effect of coatings on oxidation behavior of a fourth generation Ni-based single crystal superalloys at ultra high temperature