Improved microstructures and mechanical properties for 7085Al alloy subjected to slow quenching by aging treatment

Hongyu Xiao,Jiwei Geng,Yugang Li,Zhiping Wang,Qing Yang,Hongping Li,Mingliang Wang,Dong Chen,Zhuguo Li,Haowei Wang

DOI: https://doi.org/10.1016/j.msea.2021.142068

2021-01-01

Abstract:The precipitation behaviors and mechanical properties of the slowly-quenched 7085Al alloy subjected to various aging treatments were studied by multi-scale microstructural and mechanical properties characterization techniques. There were coarse quench-induced precipitates (QIPs) including eta phases and lath-shaped S phases identified at grain boundaries and Al3Zr particle interfaces during the slow quenching process. Both precipitate free zone and precipitate rich zone were characterized in the slowly-quenched samples after various aging treatments. It was found that the average size of the age-induced precipitates (AIPs) after the double-step aging treatment (D3) was finer, and the number density of the AIPs was larger than those after the single-step aging treatment (S1). Meanwhile, the precipitate free zones around the coarse QIPs and at grain boundaries became narrower in the D3 sample. Critically, the heterogeneous nucleation of eta ' phase on the lath-shaped S phase which was previously unreported has been characterized. The orientation relationship between the eta' phase and S phase was determined, and the detailed mechanism was discussed based on heterogeneous nucleation theory. Furthermore, the yield strength and ultimate tensile strength of the D3 sample increased by -94.4 MPa and -65.9 MPa over the S1 sample, respectively. Finally, the underlying mechanisms of such yield strength variations were discussed. The mixture rule was used to model this microstructure-mechanical property relationship quantitatively, in which the calculated results showed the good agreement with the measured results.