Microstructure characteristics of an ultra-high strength extruded Al-4.7Cu–1Li-0.5Mg-0.1Zr–1Zn alloy during heat treatment

Jiangwei Sun,Guohua Wu,Liang Zhang,Xiaolong Zhang,Longling Liu,Jinshuo Zhang
DOI: https://doi.org/10.1016/j.jallcom.2019.152216
IF: 6.2
2020-01-01
Journal of Alloys and Compounds
Abstract:In this work, a novel Al-4.7Cu–1Li-0.5Mg-0.1Zr–1Zn alloy was designed with the purpose of developing ultra-high strength and low-cost Al–Cu–Li alloy. The mechanical properties and microstructure evolution of the studied alloy under T6, T8, and two-stage aged conditions were investigated. The alloy showed a non-recrystallization feature during solution treatment. A strong <111> fiber texture was presented in the as-quenched alloy. The yield strength (YS), ultimate tensile strength (UTS), and elongation (EL) of the alloy was largely depended on the aging process parameters. A good combination of ultra-high strength (YS = 731 MPa, UTS = 753 MPa) and ductility (EL = 5.5%) were obtained in the T8 treated specimen (pre-stretched by 3% and aged at 150 °C for 32 h). The pre-strain prior to artificial aging and aging temperature significantly affect the distribution, density, and size of precipitates. Strengthening mechanism of the alloy was discussed in detail. The strong <111> texture preserved in the as-quenched alloy and the finely dispersed T1 (Al2CuLi) phases distributed in the T8 treated specimens could account for the ultra-high strength of the present alloy.
What problem does this paper attempt to address?