Abstract:Phosphogypsum is an industrial waste generated in the production of fertilizers causing environmental problems. Calcined phosphogypsum (CPG) is obtained by low-temperature calcination and dehydration of phosphogypsum. CPG is mainly used to produce building materials. However, mechanical strength properties and water resistance of CPG materials is extremely poor, which leads to its relatively low utilization rate in construction industry. To address this issue, various amount of Ordinary Portland cement (OPC), fly ash (FA), rice husk (RH) and modified admixtures (AD) were mixed with the CPG to obtain CPG-based composite cementitious materials, which enhanced the water resistance and mechanical strength of the corresponding hardened materials. The influence of different contents of cement on the setting time, hydration heat, hydration products, mechanical properties, water absorption, heavy metal leaching and deterioration coefficient of the composite cementitious material is investigated. The results showed that the optimal mixing ratio of CPG: OPC: FA: RH was 57: 20: 10: 13 considering the water resistance and mechanical strength properties of CPG-based composite cementitious materials. On these conditions, the compressive strength, the flexural strength, water absorption and deterioration coefficient of the specimens at 28 days are 6.1 MPa, 4.6 MPa, 29.4% and 0.66 respectively, which were in line with the national standard of phosphorus building gypsum wallboard. It was demonstrated that two skeleton types are present in the samples prepared using CPG-based composite cementitious materials, which had a synergistic support effect on the structure. The first skeleton was formed by gypsum dihydrate crystals (CaSO 4 ·2H 2 O) and provided strength to the specimens at an early stage, while the second skeleton was formed by ettringite (AFt) and C–S–H gels, which provided strength at a later stage. The skeletons make the hardened materials denser and more waterproof. Moreover, the composite materials exhibited a positive solidification effect on heavy metals present in CPG.

Laboratory Investigation of Cemented Silt Improved with Bentonite and Phosphogypsum in DCM Walls

Stabilization Nature and Unified Strength Characterization for Cement-Based Stabilized Soils

Study on Mechanism of Muddy Soil Stabilization

Sedimentation-affected Engineering Performances and Microstructures of a Hybrid Portland- Sulfate Aluminate Cement Grout Cast in Long Tubes

Laboratory Experiment on Formation of MICP Horizontal Seepage-Reducing Body in Confined Aquifer for Deep Excavation

Experimental Study on Mechanical Properties of Soft Clay Stabilized by Industrial By-Products

Mechanical and microstructural properties of cement-treated marine dredged clay with red mud and phosphogypsum

Strength performance and enhancement mechanism of silty sands stabilized with cement, red mud, and phosphogypsum

Use of recycled gypsum in the cement-based stabilization of very soft clays and its micro-mechanism

Using alkali-activated dredge sludge ash-bentonite for low permeability cutoff walls: The engineering properties and micromechanism

Micro-macro investigation on bio-cemented sand under different grouting saturation: an effective enhancement method

Cement-SG curing agent for solidification of mucky soils

Strength and Permeability of Bentonite-Assisted Biocemented Coarse Sand

Experimental Study of Solidification of Dredged Clays with High Water Content by Adding Cement and Phosphogypsum Synchronously

Al2O3/SO3 molar ratio of PG-CAC-based binders on the macro-micro properties of cement-treated waste dredged clay

Collaborative effects of red mud and phosphogypsum on geotechnical behavior of cement-stabilized dredged clay

Mechanical and microstructural properties of silt roadbed filling improved with cement, red mud and desulfurization gypsum

The effects of desulfurized gypsum on the mechanical properties of dredged clay with high initial water content stabilized by ternary geopolymer

Investigation on properties and mechanism of non-calcined Bayer red mud-phosphogypsum cementitious binder

Comparative research on the application of slag as an alternative to cement in binder-bentonite cutoff wall backfills

Influence of cement on properties of calcined phosphogypsum based composite cementitious materials