Effect of Annealing on the Microstructure, Texture, and Properties of Cold-Rolled Ti50Ni47Fe3 Shape Memory Alloy Sheets
Shuwei Liu,Xiaoyun Song,Yanfeng Li,Yang Yu,Wenjun Ye,Songxiao Hui
DOI: https://doi.org/10.3390/cryst14040360
IF: 2.7
2024-04-12
Crystals
Abstract:A systematic study was conducted on the impact of annealing treatments on the microstructure and properties of cold-rolled Ti50Ni47Fe3 alloys using optical microscopy, scanning electron microscopy, electron backscattered diffraction, and an electronic universal testing machine. It was found that, during low-temperature annealing (400 °C and 500 °C), the annealing time had no significant effect on the microstructure or properties of the Ti50Ni47Fe3 alloy. Only elongation (δ) increased with the increase in the annealing time, and the grain orientation of the Ti50Ni47Fe3 alloy was //RD (rolling direction). When annealing at medium–high temperature (600 °C), as the annealing time increased, recrystallization and grain growth processes occurred, resulting in a continuous decrease in strength and an increase in δ. Meanwhile, it was found that the grain orientation of the cold-rolled Ti50Ni47Fe3 alloy changed from //RD during the recovery and recrystallization processes to //RD after the grain growth process. The orientation distribution function cross-section φ2 = 45° results indicate that the texture was mainly distributed along the γ orientation line (φ1 = 0~90°, Φ = 54.7°, φ2 = 45°). When annealed at 400 °C and 500 °C, the texture of the Ti50Ni47Fe3 alloys was (111)[uvw]. When the annealing treatment was 600 °C for 120 min, a (110)[uvw] texture occurred. Additionally, ductile fracture occurred in all specimens, and the crack origin was located on one side of the fracture surface, with obvious "Y"-shaped propagation. This article studied annealing treatments of cold-rolled Ti50Ni47Fe3 alloys, providing corresponding theoretical guidance for subsequent production applications.
materials science, multidisciplinary,crystallography