The shape memory effect and corrosion resistance of the Ti-35wt%Nb alloy

Yanbo Wang,Benli Wang,Li Li.,Yufeng Zheng
2005-01-01
Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering
Abstract:Ti-35wt%Nb alloy was fabricated by arc melting method. The ingots were hot-rolled to ∼1.2 mm plate and then solution treated at 850°C for 30 min and then water quenched. XRD analysis results revealed that two kinds of phases (β+α″) were presented, and two different kinds of textures were observed from the optical micrographs. Shape memory effect was investigated by the bending equipment designed by us, and the results revealed that the strain should be less than 4.4% in order to obtain the maximum shape recovery ratio. The corrosion resistance of the Ti-35%Nb alloy in Hank's and Saliva solution with different pH values at 37°C was investigated by electrochemical method, the Ti-35%Nb alloy has a better corrosion resistance in Saliva solution with the same pH value 7.4.