Synthesis And Characterization Of La1-Xcaxfeo3-Delta For Cathodes By Gnp Method

Yh Chen,Yj Wei,Xq Liu,Gy Meng

2005-01-01

Chinese journal of inorganic chemistry

Abstract:LaFeO3 and La1-xCaxFeO3-(delta) with 0.1 <= x <= 0.5 were synthesized using glycine-nitrate process (GNP). The formation process of perovskite phase and microstructure of the samples were characterized using TG-DTA, XRD, and SEM. The results revealed that fine powders with particle size of 50 similar to 90 nm were obtained. All the samples with different doping amounts of Ca2+ on A-site were single phase solid solutions, and the stable perovskite phase was formed completely after calcination at 850 T. The solid solutions with 0.0 <= x <= 0.2 were isostructural with the orthorhombic perovskite-type LaFeO3, while those with composition of 0.3 <= x <= 0.5 were the cubic perovskite-type system. The diffraction intensity, the cell volume as well as grain size of products decreased with Ca content. The electrical conductivity of sintered samples as a function of both temperature and Ca content were measured by four-probe technique. The Ca doped on A-site of LaFeO3 had a significant effect on electrical properties. The electrical conductivity increased as Ca content and then decreased, La0.6Ca0.4FeO3-delta was found to be of the highest conductivity. The activation energy of La1-xCaxFeO3-delta (0.1 <= x <= 0.5) was 13.67 similar to 22.70 kJ circle mol(-1), while that of LaFeO3 was 100.89 kJ circle mol(-1).