Synthesis and characterization of La1-xCaxFeO 3-δ for cathodes by GNP method

Yonghong Chen,YiJun Wei,Xingqin Liu,Guangyao Meng

2005-01-01

Chinese journal of inorganic chemistry

Abstract:LaFeO3 and La1-xCaxFeO3-δ with 0.1 ≤ x ≤ 0.5 were synthesized using glycine-nitrate process (GNP). The formation process of perovskite phase and microstructure of the samples were characterized using TG-DTA, XRD, and SEM. The results revealed that fine powders with particle size of 50-90 nm were obtained. All the samples with different doping amounts of Ca2+ on A-site were single phase solid solutions, and the stable perovskite phase was formed completely after calcination at 850°C. The solid solutions with 0.0 ≤ x ≤ 0.2 were isostructural with the orthorhombic perovskite-type LaFeO3, while those with composition of 0.3 ≤ x ≤ 0.5 were the cubic perovskite-type system. The diffraction intensity, the cell volume as well as grain size of products decreased with Ca content. The electrical conductivity of sintered samples as a function of both temperature and Ca content were measured by four-probe technique. The Ca doped on A-site of LaFeO3 had a significant effect on electrical properties. The electrical conductivity increased as Ca content and then decreased, La0.6Ca 0.4FeO3-δ was found to be of the highest conductivity. The activation energy of La1-xCaxFeO 3-δ (0.1 ≤ x ≤ 0.5) was 13.67-22.70 kJ·mol -1, while that of LaFeO3 was 100.89 kJ·mol -1.