Synthesis and Characterization of Pr_(0.6-x)Nd_xCa_(0.4)FeO_(3-δ) with Pechini Method

Chen Yonghong,Chu Zhaorong,Wei Yijun,Liu Xingqin,Meng Guangyao

2006-01-01

Abstract:Pr_(0.6-x)Nd_xCa_(0.4)FeO_(3-δ)(x=0.0,0.2,0.3,0.4,0.5,0.6) were synthesized using Pechini method.A number of studies were conducted concerning composition,specific area,crystalline structure and microstructure of the samples by means of FT-IR,BET,XRD TG-DTA and SEM.The results show that all the samples with different doping amounts of Pr~(3+) and Nd~(3+) on A-site are fine dispersed,and mean particle size less than 100 nm.The powders have good sinterability,and the relative density is 95% after sintered at 1200 ℃ for 2 h.It is found that all specimens are entirely single phase solid solutions with orthorhombic perovskite structure,the stable perovskite-type phase is formed completely after calcination at 900 ℃.It has no effect on crystalline structure for two rare earths on A-site of ABO_3.The width of diffraction peak increases with Nd contents.The electrical conductivity of sintered samples as a function of both temperature and Nd content was measured by four-probe technique,and the electrical properties of two rare earths-boaring samples are prior to ones with single rare earth.Pr_(0.1)Nd_(0.5)Ca_(0.4)FO_(3-δ) is found to be of the highest conductivity.