Abstract:Hyperbranched polyethylene (HBPE) is a new type of polyethylene materials in addition to low-density polyethylene (LDPE), high-density polyethylene (HDPE), and linear low-density polyethylene (LLDPE). It has dendrimer-like compact globular structures. Due to lack of chain entanglements, it exhibits better solubility and lower viscosity than the other types of polyethylene. HBPE has attracted great attention in the recent years in both academic and industrial researches. However, as polyolefin materials, HBPE suffers from such shortcomings as nonpolar nature and thus lack of functionalities. These shortcomings limit its applications. Grafting of polar molecules such as maleic anhydride (MAH) has been widely adopted in the modification of polyolefins.In this work, HBPE samples having high molecular weight (M-w = 8 x 10(6) g/mol) and high branching density (the number of branches per 1000C = 108) were synthesized by solution polymerization of ethylene with a late transition metal catalyst, namely bi (2, 6-diispropylphenyl) butane diimine nickel dibromide (IBNB) at 45 degrees C and 0.5 MPa. The Ni catalyst is well-known to experience a chain walking mechanism that is responsible for the hyperbranched chain topology. H-1-NMR and C-13-NMR were used to examine the branching density and the type of branches, respectively. It was discovered that the types of branches were mainly methyl (50.54 %) and butyl (20.30%).MAH was grafted onto HBPE through a free radical mechanism. Di-tert amyl peroxide (DTAP) was used as the free radical initiator. However, it was found that the HBPE/MAH/DTAP grafting system experienced severe chain degradation and crosslinking side reactions during the grafting process. N, N-diethyl cinnamamide (DECA) was thus synthesized by the use of cinnamoyl chloride, diethylamine, and triethylamine which was used as an acid-binding reagent. DECA was then used as an inhibitor to suppress the side reactions. The approach was successful and efficient. The gel content in the grafting products was remarkably reduced from 55.38% to 5.15%. The M. was almost doubled in reference to the use of MAH and peroxide DTAP only. The observation suggests that the chain degradation and crosslinking side reactions were dramatically suppressed with the addition of DECA.Compared to the other investigated inhibitors such as styrene (St), N, N-dimethylacetamide (DMAC), 3-(2-furyl) acrylic acid (FAA) and ethyl cinnamate (ECA), DECA was found to be the most effective in suppressing both chain degradation and crosslinking side reactions. We also found that FAA and ECA could effectively suppress the chain degradation in the grafting system, but the grafting system had high gel contents and experienced severe crosslinking. St and DMAC had some effects on inhibiting crosslinking, but there was still small amount of crosslinking. The proposed mechanism is that DECA reacts first with HBPE macroradicals to form stable macroradicals when DECA is added to the grafting system. The latter then reacts (or copolymerizes) with MAH to form MAH-grafted HBPE. Because the formed stable macromolecules contain amide group, both the chain degradation and crosslinking side reactions are effectively suppressed.In general, in the presence of radical initiator, HDPE mainly experiences crosslinking, while polypropylene undergoes chain scission. LDPE and LLDPE have both reactions simultaneously occurring. HBPE is more or less similar to the low-density materials having simultaneous crosslinking and degradation. In the grafting studies, these side reactions need to be controlled. The current work elucidates the grafting mechanisms and provides practical guidance in this regard.

Surface Grafting of Phenolic Resole Onto Ldpe Films

Surface Grafting of Resorcinol Onto Polyethylene Film

Two-step surface grafting of acrylic acid on low density polyethylene(LDPE) film initiated by fluorenone

GRAFTING OF MALEIC ANHYDRIDE ONTO HYPERBRANCHED POLYETHYLENE AND SUPPRESSION OF CHAIN DEGRADATION AND CROSSLINKING SIDE REACTIONS

Controlled Grafting of Comb Copolymer Brushes on Poly(tetrafluoroethylene) Films by Surface-Initiated Living Radical Polymerizations.

PHOTOGRAFTING OF HSS ON THE SURFACE OF LDPE FILM BY TWO STEPS

Fluorinated acrylate-grafted LDPE films from UV-induced photograft polymerization

SURFACE PHOTOGRAFTING OF FUNCTIONAL MONOMERS INITIATED BY FLUORENONE ON LDPE FILMS

Preparation and Chracaterization of Novel Graft Copolymers of LLDPE

Surface Photografting Polymerization Of Trimethylolpropane Triacrylate Onto Ldpe Substrate In Tetrahydrofuran/Water Mixtures

Surface Modification of Low-Density Polyethylene Films Via Photografting Polymerization Technique

A Facile Method for Grafting Polymerisation of Acrylonitrile onto LDPE Film with High Grafting Efficiency

Surface Graft Polymerization of Glycidyl Methacrylate Onto Polyethylene and the Adhesion with Epoxy Resin

Preparation and Properties of a Reactive Type Nonionic Surfactant Grafted Linear Low Density Polyethylene

Synthesis and Characterization of Linear Low Density Polyethylene Grafted Glycerol Monolauric Acid Monoitaconic Acid Diester

Surface Photograft Polymerization of Vinyl Acetate on Low Density Polyethylene Film. Effects of Solvent

Grafting Polymerization of Acrylonitrile onto LDPE Film: Study on Grafting Chain Length and Density with UV-vis Spectroscopy

Surface Modification of Poly(tetrafluoroethylene) Films Via Plasma Treatment and Graft Copolymerization of Acrylic Acid

STUDIES ON PHOTOGRAFTING OF TRIMETHYLOL PROPANE TRIACRYLATE ONTO THE SURFACE OF LDPE FILMS

Efficient Approach for Direct Robust Surface Grafting of Polyethyleneimine onto a Polyester Surface during Moulding