Effects Of Ultrasound On The Microstructures And Mechanical Properties Of Cast-Rolling Az3b Magnesium Alloy Strip

Li Jianping,Hu Jianbing,Mao Daheng,Zhao Guanzhong

DOI: https://doi.org/10.4028/www.scientific.net/MSF.686.129

2011-01-01

Abstract:The experiment of ultrasonic cast-rolling magnesium strip was carried out on the horizontal twin-roll cast-rolling machine with the ultrasonic pole used in the solidification. The microstructures of ultrasonic and general cast-rolling magnesium strip were characterized. The results showed that the cellular dendrite of the general cast-rolling magnesium strip was coarse, the grain structure was heterogeneous and the average grain diameter was between 50 mu m similar to 60 mu m. However, the grain structure became more homogenize after the ultrasonic treatment for cast-rolling magnesium strip, the grain was refined and the average grain diameter was between 20 mu m similar to 30 mu m. Besides, the mechanical properties test results show that the tensile strength, yield strength and elongation of the ultrasonic cast-rolling magnesium strip were increased by 22.85%, 49.78% and 123.06% than those of the general cast-rolling magnesium strip.