Effect of Hot-Rolling and Warm-Rolling Process on Properties of Cast-Rolling AZ31B Magnesium Alloy Strip
Daheng Mao,Biao Zhang,Jianping Li,Zhipeng Li,Chen Shi
DOI: https://doi.org/10.1016/j.proeng.2011.12.535
2012-01-01
Procedia Engineering
Abstract:The effect of different temperature, passes and deformation rates of rolling process on the microstructure and mechanical properties of general cast-rolling magnesium strip and compound energy-field (electromagnetic field and ultrasonic wave) cast-rolling magnesium strip were investigated. The results of microstructure observation showed that the recrystallized temperature in compound energy-field cast-rolling magnesium strip was lower than those of the general cast-rolling magnesium strip. When rolling at 250°C, the recrystallization of general cast-rolling magnesium strip was not remarkable, while the compound energy-field cast-rolling magnesium strip's local recrystallization was observed; while in the case of rolling temperature of 300°C, the general cast-rolling magnesium strip shows local recrystallization and remarkable fibrous structure, while the compound energy-field cast-rolling magnesium strip was fully recrystallized, and the grain became finer and uniform; rolling at 400°C, both general cast-rolling magnesium strip and compound energy-field cast-rolling magnesium strip were fully recrystallized. The results of EDS analysis showed that precipitates of general cast-rolling magnesium strip were numerous and concentrated in and near the grain boundary, while the precipitates of compound energy-field cast-rolling magnesium strip were few and dispersed in the grain boundary in small particles. The results of mechanical properties measurement showed that the σb,σ0.2 and δ of compound energy-field cast-rolling magnesium strip enhanced by 11%, 22.2%, 145% and 13.6%, 19.7%, 127.8%, respectively, compared to general cast-rolling magnesium strip after three rolling passes at the rolling temperature of 250°C and 300°C.