Abstract:The effect of annealing temperature and time on the microstructure and mechanical properties of AZ31B Mg alloy sheets were investigated. The specimens were deformed by general roll-casting and combining energy-field roll-casting (electromagnetic field and ultrasonic). The microstructure analysis showed that the re-crystallization temperature of combining energy-field Mg sheet was lower than that of general Mg sheet. It has been found that at the annealing of 250°C, no obvious re-crystallization occurred for the general Mg strip sheet, while the local re-crystallization occurred for the Mg strip sheet with combining energy-field roll-casting. However, in the condition of annealing at 300°C, the specimens of roll-casting Mg strips fully re-crystallized with the holding time of 4h, and the specimens with compound energy-field Mg strip had fine grains and uniform microstructure, and the average grain diameter were 14∼19μm, 8∼13μm for the general Mg strip sheet and combining energy-field Mg strip sheet, respectively. When the specimens were annealed at 400°C, the grains became coarse within 1h, the average grains diameters were 20∼25μm and 28∼33μm respectively for the general Mg roll-casting sheet and combining energy-field Mg roll-casting sheet when annealing at 400°C for 1h. The results of EDS showed that the precipitates amount of annealed Mg roll-casting sheets were reduced by annealing, the precipitates of general Mg roll-casting sheet with thicker size were enriched on the grain boundaries. The results of the mechanical properties indicated that the plastic deformation of roll-casting Mg sheets was improved significantly; Under the annealing condition of 300°C × 4h, the values of HBS, σb, σ0.2 and δ of combining energy-field Mg strip were improved by 4.7%, 17.2%, 34.1%, 74.6%, compared to general Mg sheet.

Effect of Composite Energy-Field on Microstructure and Properties of Az31b Magnesium Roll-Casting Alloy Sheet

Effects of Compound Energy Field on Microstructure and Mechanical Properties of Roll-Casted AZ61 Magnesium Alloy Strip

Effect of Compound Energy-Field with Ultrasonic and Electromagnetic Field on Microstructure and Mechanical Properties of Roll-Casted 1060 Aluminum Alloy Strip

Experimental Study of Electromagnetic Roll-casting for AZ31B Magnesium Alloy

Effects of ultrasonic and electromagnetic field on structure and properties of roll-casting 1050 aluminium alloy strips

Research of Ultrasound and Electromagnetic Field on the Microstructure of Cast-Rolling Magnesium Strip

Effect of Ultrasonic Wave on Solidified Structure and Mechanical Properties of AZ31B Magnesium Alloy

Experimental Study on Twin-roll Casting Magnesium Alloy Strip

Effect of Hot-Rolling and Warm-Rolling Process on Properties of Cast-Rolling AZ31B Magnesium Alloy Strip

Effect of Ultrasonic/Electromagnetic Energy-Field on Structure Andproperties of Cast-Rolled 3003 Aluminum Alloy Strips

An Effective Approach Called the Composite Extrusion to Improve the Mechanical Properties of AZ31 Magnesium Alloy Sheets

Effect of Annealing Process on Microstructure and Properties of Roll-Casting AZ31B Mg Alloy Sheet

Effects of Ultrasound on the Microstructures and Mechanical Properties of Cast-Rolling AZ31B Magnesium Alloy Strip

Effects of Ultrasonic Vibration on Microstructure and Properties of As-Cast and Hot Rolled AZ31 Magnesium Alloy

Evolution of microstructure and texture of electromagnetic and ultrasonic energy-field cast-rolling AZ31B Mg alloy sheet during subsequent warm-rolling process

Effect of Hot Extrusion on Microstructure and Mechanical Properties of Electromagnetic Continuous Cast Az31 Magnesium Alloy

Effect of Electromagnetic Fields on Microstructure and Mechanical Properties of Sub-Rapid Solidification-Processed Al–Mg–Si Alloy During Twin-Roll Casting

Effects Of Ultrasound On The Microstructures And Mechanical Properties Of Cast-Rolling Az3b Magnesium Alloy Strip

Effect of Rolling Method on Microstructure and Properties of AZ31 Magnesium Alloy Thin Sheet

Experiment research on ultrasound cast-rolling AZ31 alloy strip

A Fine Microstructure Of Az31 Magnesium Alloy Developed By Composite Extrusion In Solid-Liquid Two-Phase Region