Abstract:High purity magnesium and a Mg-Al 5wt% Zn metal rich primer (MRP) were compared for their ability to suppress intergranular corrosion (IGC) and intergranular stress corrosion cracking (IG-SCC) in peak aged AA 7075-T651 by sacrificial anode-based cathodic prevention. Tests were conducted in 0.6 M NaCl solution under full immersion. These evaluations considered the ability of the primer to attain an intermediate negative open circuit potential (OCP) such that the galvanic couple potential with bare aluminum alloy (AA) 7075-T651 resided below a range of potentials where IGC is prevalent. The ability of the primer to achieve an OCP negative enough that the AA 7075-T651 could be protected by sacrificial anode-based cathodic prevention and the ability to sustain this function over time were evaluated as a first step by utilizing a NaCl solution. The primers consisted of epoxy resins embedded with either (1) Mg flake pigments (MgRP) or (2) Mg flake pigments and spherical Al-5 wt.% Zn together as a composite (MgAlRP). MgRP was an effective coating for cathodic protection but dispensed less anodic charge than the composite MgAlRP. Cross-sectional analysis demonstrated that some Mg flakes dissolved while uniform surface oxidation occurred on the remaining Mg flakes which led to impaired activation. The composite MgAlRP maintained a suitably negative OCP over time, remained activated, dispensed high anodic charge, and remained an anode in zero resistance ammeter testing. Chemical stability modeling and zero resistance ammeter testing suggest that Mg corrosion elevates the pH which dissolved aluminum oxides and hydroxide thereby activates the Al-5wt.% Zn pigments, thereby providing a primary (i.e. Mg corrosion) and secondary process to enable superior (activation of Al-5wt%Zn) sacrificial anode-based cathodic protection.

Surface Characterisation Of Rapidly Solidified Mg-Based Alloys Immersed In 3%Nacl Solution

Characterization of corrosion products formed on a rapidly solidified Mg based EA55RS alloy

Effect of alloying addition of Pr on the dissolution rate of melt-spun Mg in 3% NaCl solution

Study of the Corrosion Product Films Formed on the Surface of Mg–xZn Alloys in NaCl Solution

Corrosion Behaviour of Aluminium-Magnesium Alloys in Molten Sodium

Investigation of Corrosion Behaviors of Mg–6Gd–3Y–0.4Zr Alloy in NaCl Aqueous Solutions

Characterisation of Li in the surface film of a corrosion resistant Mg-Li(-Al-Y-Zr) alloy

Characterization of Anodic Coating Formed on Mg-3Nd-0.2Zn-0.4Zr Mg Alloy in Alkaline Electrolyte

Investigations on Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn-Zr-Nd Alloy

The Corrosion Behaviors of Mg–7Gd–5Y–1Nd–0.5Zr Alloy under (NH4)2SO4, NaCl and Ca(NO3)2 Salts Spray Condition

Corrosion Behavior of Mg-Zn-Y-Zr Alloys in Nacl Solution

Microstructure and Corrosion of Cast Magnesium Alloy ZK60 in NaCl Solution

Electrochemical Evaluation of Mg and a Mg-Al 5%Zn Metal Rich Primers for Protection of Al-Zn-Mg-Cu Alloy in NaCl

Determination of corrosion product film on pure Mg in Cl − environment using XPS etching

Comparative Study on Corrosion Behavior of As-Cast and Extruded Mg–5Y–7Gd–1Nd–0.5Zr Alloy in 5% NaCl Aqueous Solution

Influence of NaCl Deposition on Atmospheric Corrosion Behavior of AZ91 Magnesium Alloy

Microstructure and Salt Fog Corrosion of Wrought Mg-Al-Zn and Mg-RE Alloys

Dissolution of Mg-based Mg–Ni–Nd amorphous alloys in 3% NaCl solution

In-situ AFM and quasi-in-situ studies for localized corrosion in Mg-9Al-1Fe-(Gd) alloys under 3.5 wt.% NaCl environment

High-frequency induction for surface alloying of magnesium alloy ZM5 and its corrosion behavior

Corrosion Behavior and Surface Modification of Mg-Zn Implant Alloys