Abstract:Surface-enhanced Raman scattering is an effective analytical method that has been intensively applied in the field of identification of organic molecules from Raman spectra at very low concentrations. The Raman signal enhancement that makes this method attractive is usually ascribed to the noble metal nanoparticle (NMNP) arrays which can extremely amplify the electromagnetic field near NMNP surface when localized surface plasmon resonance (LSPR) mode is excited. In this work, we report a simple, facile, and room-temperature method to fabricate large-scale, uniform gold nanoparticle (GNP) arrays on ITO/glass as SERS substrates using a promoted self-assembly deposition technique. The results show that the deposition density of GNPs on ITO/glass surface increases with prolonging deposition time, and nanochain-like aggregates appear for a relatively longer deposition time. It is also shown that these films with relatively higher deposition density have tremendous potential for wideband absorption in the visible range and exhibit two LSPR peaks in the extinction spectra because the electrons simultaneously oscillate along the nanochain at the transverse and the longitudinal directions. The SERS enhancement activity of these GNP arrays was determined using 10-6 M Rhodamine 6G as the Raman probe molecules. A SERS enhancement factor as large as approximately 6.76 × 106 can be obtained at 1,363 cm-1 Raman shift for the highest deposition density film due to the strong plasmon coupling effect between neighboring particles.

Si-Nw Arrays Decorated With Gold Nanoparticles For Surface-Enhanced Raman Scattering

Surface-enhanced Raman scattering from rhodamine 6G on gold-coated self-organized silicon nanopyramidal array

Hybrid Metal-Insulator-metal Structures on Si Nanowires Array for Surface Enhanced Raman Scattering

Aligned Gold Nanoneedle Arrays for Surface-Enhanced Raman Scattering

Gold/Silicon Nanowire Arrays Modified by Gold Nanosphere As the Surface-Enhanced Raman Spectroscopy Substrate

Gold nanoparticle-coated silicon cone array for surface-enhanced Raman spectroscopy

Ultrasensitive Surface-Enhanced Raman Scattering Based Gold Deposited Silicon Nanowires

3D Surface-Enhanced Raman Scattering Substrate Based on an Array of Self-Assembled Au@SiO2 Microspheres

A High-Efficiency Surface-Enhanced Raman Scattering Substrate Based on Silicon Nanowires Array Decorated with Silver Nanoparticles

Single Gold-Nanoparticles-Decorated Silver/Carbon Nanowires As Substrates for Surface-Enhanced Raman Scattering Detection

Large-Area Au-Nanoparticle-Functionalized Si Nanorod Arrays for Spatially Uniform Surface-Enhanced Raman Spectroscopy.

Surface-Enhanced Raman Scattering from Uniform Gold and Silver Nanoparticle-Coated Substrates

Aligned Silver Nanorod Arrays for Surface-Enhanced Raman Spectroscopy

Integrate silver colloids with silicon nanowire arrays for surface-enhanced Raman scattering

High Aspect Ratio Sinw Arrays with Ag Nanoparticles Decoration for Strong Sers Detection

Silicon nanowire arrays coated with electroless Ag for increased surface-enhanced Raman scattering

Surface-enhanced Raman scattering of rhodamine 6G on nanowire arrays decorated with gold nanoparticles.

Self-assembly of Large-Scale Gold Nanoparticle Arrays and Their Application in SERS

Preparation of Gold Nano-Cones As Surface-Enhanced Raman Scattering Sensors for Molecule Detection.

Fabrication of silver-coated silicon nanowire arrays for surface-enhanced Raman scattering by galvanic displacement processes

Silver Nanoparticle-Decorated Silica Nanospheres and Arrays as Potential Substrates for Surface-Enhanced Raman Scattering