Abstract:Recently, metallic nanoparticles decorated semiconductor nanowires, especially silicon, attract considerable attention, due to their potential applications in photocatalysis, photovoltaics, surface enhanced Raman scattering and biosensing. A common method that has been used to decorate silicon nanowires with metallic nanoparticles, e.g. Au or Pt, is galvanic displacement, in which metallic ions are reduced with electrons supplied by virtue of silicon half-cell reaction. Here we report a method to decorate silicon nanowires with Ag nanoparticles by surface reduction, in which a freshly etched silicon surface reduces Ag ions in-situ in aqueous silver nitrate solution. The as-grown Ag nanoparticles exhibit either highly single crystallinity or twinning boundaries, with most probably diameter similar to 25 nm (Figure 1). Raman mapping experiments suggest that 1(st) order Raman band of silicon nanowires exhibit uniform contrast along wire axis for pristine silicon nanowires, while for Ag nanoparticle decorated silicon nanowires a series of "hot-spot", i.e., substantially enhanced Raman scattering were discovered along the wire axis. This was explained by local electric field enhancement due to Ag nanoparticle "nano-antenna", which was supported by the correlation between atomic force microscopy (AFM) analysis and Raman mapping (Figure 2). The enhancement is more or less delocalized in Raman mapping due to diffraction limit in our far-field mapping experiments. In addition, we also noticed a new side band feature similar to 495 cm(-1) for nanowires appeared after HF etching, this new feature sustained after sequential Oxygen plasma and UV/ozone treatment which excluded the possibility due to any possible surface dangling bonds. We now suspect this feature is due to porosity resulted from HF etching and it is now being subjected to further investigations.

Fabrication of silver-coated silicon nanowire arrays for surface-enhanced Raman scattering by galvanic displacement processes

Metallization of Silicon Nanowires and Sers Response from A Single Metallized Nanowire

Electrochemical synthesis of silver oxide nanowires, microplatelets and application as SERS substrate precursors

Electrochemically Prepared Porous Silver and Its Application in Surface-Enhanced Raman Scattering

Integrate silver colloids with silicon nanowire arrays for surface-enhanced Raman scattering

Fabrication of High Performance Surface Enhanced Raman Scattering Substrates by a Solid-State Ionics Method

Fabrication of Ag Films Composed of Close-Packed Nanoparticles and Their Surface-Enhanced Raman Scattering Effects

Hybrid Metal-Insulator-metal Structures on Si Nanowires Array for Surface Enhanced Raman Scattering

Si-Nw Arrays Decorated With Gold Nanoparticles For Surface-Enhanced Raman Scattering

Facile Fabrication of Silver Nanoparticles on Silicon for Surface‐enhanced Infrared and Raman Analysis

Single-crystal silver nanowires: Preparation and Surface-enhanced Raman Scattering (SERS) property

Fabrication and characterization of polycrystalline silicon nanowires with silver-assistance by electroless deposition

Silver Nanocrystals: Synthesis and Surface-Enhanced Raman Spectroscopy

The preparation of silver nanoparticle decorated silica nanowires on fused quartz as reusable versatile nanostructured surface-enhanced Raman scattering substrates

Surface-enhanced Raman scattering from silver nanostructures with different morphologies

Silver catalysis in the fabrication of silicon nanowire arrays

Enhanced Raman Scattering of Silicon Nanowires by Ag Nanoparticles in‐situ Decoration

The Kinetically Dominated Overgrowth of Flower-Like Silver Nanostructures and Its Application for Surface-Enhanced Raman Scattering

Surface-enhanced Raman Scattering from Different Silver Nanostructures

Shape-diversified silver nanostructures on Al foil fabricated in micellar template for high performance surface enhanced Raman scattering applications

Gold/Silicon Nanowire Arrays Modified by Gold Nanosphere As the Surface-Enhanced Raman Spectroscopy Substrate