Abstract:Due to the poor activation performance and kinetics of Ti50V25Cr25 alloys, the element Zr was added to improve the phase structure of the alloy and achieve a high-performance hydrogen storage alloy. The Ti50-xV25Cr25Zrx (x = 0, 5, 7, and 9) system alloys were prepared by arc melting. The alloys were analyzed using an X-ray diffractometer (XRD), scanning electron microscope (SEM), and differential scanning calorimeter (DSC). The hydrogen storage capabilities of the alloys were also obtained by the Sievert volumetric method. The results indicated that the alloy with Zr added had a combination of the C15 Laves phase and the BCC phase, whereas the Zr-free alloy had a BCC single phase. The partial replacement of Zr with Ti resulted in an increase in the lattice parameters of the main phase. The hydrogen storage kinetic performance and activation of the alloys both significantly improved with an increasing Zr concentration. The time to reach 90% of the maximum hydrogen storage capacity decreased to 2946 s, 230 s, and 120 s, respectively, with the increases in Zr concentration. The initial hydrogen absorption content of the alloys increased and then decreased after the addition of the element Zr. The second phase expanded with an increasing Zr concentration, which in turn decreased the abundance of the BCC main phase. The Ti43V25Cr25Zr7 alloy showed good cycle stability and hydrogen-desorption performance, and it could absorb 90% of the maximum hydrogen storage capacity in around 230 s. The maximum hydrogen-absorption capacity of the alloy was 2.7 wt%. The diffusion activation energy of hydrogen desorption dropped from 102.67 kJ/mol to 92.62 kJ/mol.

Microstructural Characterization and Hydrogenation Properties of Non-Stoichiometric Zr0.9TixV2 Alloys

Effect of zr content on the microstructures and hydrogen storage properties of (Ti-Cr)(45-x)V55Zrx (x=1 similar to 7) alloys

Effect of hypo-stoichiometry on microstructure and hydrogenation behaviors of multiphase ZrTi0.1V2- alloys

Development of Ti–Zr–Mn–Cr-(V–Fe) Based Alloys for Hydrogen Feeding System in Hydrogen Metallurgy Application

Effect of Zr Content on the Microstructures and Hydrogen Storage Properties of (Ti-Cr)_(45-x)V_(55)Zr_x(x=1～7) Alloys

Study on the modification of Zr-Mn-V based alloys for hydrogen isotopes storage and delivery

Development of Ti0.85Zr0.17(Cr-Mn-V)1.3Fe0.7-based Laves Phase Alloys for Thermal Hydrogen Compression at Mild Operating Temperatures

Microstructure and hydrogen storage properties of Ti10V84-xFe6Zrx (x = 1-8) alloys

Influence of Zr Addition on the Microstructure and Hydrogenation Kinetics of Ti50-xV25Cr25Zrx (x = 0, 5, 7, and 9) Alloys

Phase Structure and Hydrogen Storage Properties of Ti17cr23v55-Xzr5fex (X=11 Similar to 16) Alloys

Phase Structures and Electrochemical Properties of V2.1TiNi0.4Zrx (x=0−0.06) Hydrogen Storage Electrode Alloys

Microstructure and hydrogen storage properties of Ti10+xV80-xFe6Zr4 (x=0~15) alloys

MICROSTRUCTURES AND HYDROGEN STORAGE PROPERTIES OF Ti0.7Zr0.3(Cr1-xVx)2 ALLOYS

Phase Structures and Hydrogen Storage Properties of TiV1.35Cr1.35-xMnx Alloys(x=0～0.45)

Hydrogen storage capabilities of the alloys Fe 0.85Mn 0.15Ti 0.9M 0.1 (M=Zr, V, Ca)

The Effect of Cr Content on the Structural and Hydrogen Storage Characteristics of Ti10V80−xFe6Zr4Crx (x = 0–14) Alloys

Influence of Heat Treatment on the Microstructure and Hydrogen Storage Properties of Ti10V77Cr6Fe6Zr Alloy

Microstructures and Hydrogen Storage Properties of Ti10V83-xFe6ZrMnx Alloys

Effects of Ti substitution by Zr, on the microstructure and hydrogen storage properties OF Ti2-xZrxCrV (x = 0.5, 1, 1.5, 2) alloys

An Impact of Hydrogenation Phase Transformation Mechanism on the Cyclic Stabilizing Behavior of Zr0.8Ti0.2Co Alloy for Hydrogen Isotope Handling

Effect of Phase Formation on Hydrogen Storage Properties in Ti-V-Mn Alloys by Zirconium Substitution