Abstract:Selective reduction followed by magnetic or melting separation is an innovative and effective method for the comprehensive utilization of boron-bearing iron concentrate. As the raw material of boron products, the reserve of szaibelyite ore is significantly depleted. Therefore, the comprehensive utilization of boron-bearing iron ore resources becomes more and more important. To study the reduction kinetics in depth, a boron-bearing iron concentrate containing 52.18% total iron and 5.50% B2O3 was reduced isothermally with coke as the reductant. The results showed that both the reduction degree and the maximum reduction rate increased with temperature and C/O molar ratio (fixed carbon in the coke to oxygen in iron oxides in the ore). 98.00% reduction degree and 0.00414 s−1 maximum reduction rate were achieved at 1523K of reduction temperature and 1.4 of C/O molar ratio. The reduction kinetics can be best described by Avrami–Erofeev model, g(α) = [−ln(1-α)]3/2. The apparent activation energy and pre-exponential factor were 264.565 kJ·mol−1 and 1.87 × 107 s−1, respectively. The phase transformation observed by XRD agreed well with the results of reduction degree analysis. The micro-structure evolution behavior of the pellets was analyzed by SEM and EDS. As the reduction time increased from 0 to 600 s, most of the iron oxides were reduced to metallic iron, leaving other major elements in the slag phase. The slag phase mainly consisted of the solid solution of Mg2SiO4 and Mg3B2O6. With further increase to 1200 s, the metallic iron particles migrated and flocculated together forming bigger particles.

Co-Conversion Mechanisms of Boron and Iron Components of Ludwigite Ore During Reductive Soda-Ash Roasting

Extraction Of Boron From Ludwigite Ore: Mechanism Of Soda-Ash Roasting Of Lizardite And Szaibelyite

Soda-Ash Roasting Behavior of Ludwigite Ore under Different Oxygen Concentrations

Water Leaching of Boron from Soda-Ash-activated Ludwigite Ore

An integrated and efficient process for borax preparation and magnetite recovery from soda-ash roasted ludwigite ore under CO–CO2–N2 atmosphere

A Novel Process for Highly Efficient Separation of Boron and Iron from Ludwigite Ore Based on Low-Temperature Microwave Roasting

Phase Transformations and Microstructure Evolution of Boron-Containing Iron Concentrate During Roasting under CO-CO2-N2 Atmosphere: Synergistic Effect of Soda-Ash and CO Concentration

Phase Transformations and Microstructure Evolution of Soda-Ash Roasted Boron-Containing Iron Concentrate: A Comparative Investigation of Varying Roasting Atmospheres

Recovery of Powdered Metallic Iron from Ludwigite Ore Via Reductive Roasting with Sodium Salts - Magnetic Separation

An innovative process for extracting boron and simultaneous recovering metallic iron from ludwigite ore

New Separation Method of Boron and Iron from Ludwigite Based on Carbon Bearing Pellet Reduction and Melting Technology

A facile route to the value-added utilization of ludwigite ore: boron extraction and MxMg1-xFe2O4 spinel ferrites preparation

Kinetics study on the low-temperature soda roasting of boron-rich blast furnace slag

Reduction of boron-bearing iron ore concentrate/coal composite pellet and kinetics analysis

Reduction Kinetics and Microscopic Properties Transformation of Boron-Bearing Iron Concentrate–Carbon-Mixed Pellets

Recycling Excessive Alkali from Reductive Soda Ash Roasted Ludwigite Ore: Toward a Zero-Waste Approach

Synergetic Utilization of Zinc-Bearing Dust by Carbothermic Reduction-Roasting Process: Phase Transformation and Morphological Evolution

New process for treating boron-bearing iron ore by flash reduction coupled with magnetic separation

Effects of biomass reducing agent on magnetic properties and phase transformation of Baotou low-grade limonite during magnetizing-roasting

Sodium-Salt-Assisted Reductive Roasting for Separation and Enrichment of Valuable Components from Lateritic Iron Ore

Reduction and melting separation mechanism of boron-bearing iron concentrate/coal composite pellet