Abstract:The metallurgical properties of blast furnace slag changed when high alumina iron ore was used extensively due to the resulting changes of the molten slag microstructure. In the study, based on typical CaO–MgO–SiO2–Al2O3 slag systems with different w(Al2O3) content, molecular dynamics simulation was used to calculate the microstructural properties of particles in the high-temperature slag system, such as bond length, partial radial distribution function, coordination numbers, and diffusion coefficient. In addition, X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy, and 27Al solid-state magic angle spinning nuclear magnetic resonance (27Al SS MAS NMR) were used to detect and analyze the samples. The comprehensive calculations and experimental results show that increasing w(Al2O3) can enhance the structural stability of each ion pair, and the strength of the structural stability is such that Si–O > Al–O > Mg–O > Ca–O. The self-diffusion coefficients are as follows: Mg2+ > Ca2+ > Al3+ > Si4+, which leads to the transformation of the [SiO4]4−(Q0), [Si2O7]6−(Q1) and [Si2O6]4−(Q2) structural units to [Si2O5]2−(Q3). The degree of polymerization of slag increased as well as the stability of the structural units. Moreover, the coordination of Al will change from the [AlO6]9−octahedral structure of six-coordinated Al to the [AlO5]7−pentahedral structure of five-coordinated Al and the [AlO4]5−tetrahedral structure of four-coordinated Al. It was also found that the content of non-bridge oxygen in the whole slag system decreased continuously, leading to the increasing degree of polymerization of slag, and the experimental results were consistent with the molecular dynamics calculation.

Effect of Na2CO3 on reduction and melting separation of ludwigite/coal composite pellet and property of boron-rich slag

Reduction and melting separation mechanism of boron-bearing iron concentrate/coal composite pellet

New Separation Method of Boron and Iron from Ludwigite Based on Carbon Bearing Pellet Reduction and Melting Technology

Reduction of boron-bearing iron ore concentrate/coal composite pellet and kinetics analysis

The effect of coal ratio on the high-lead slag reduction process

Evaluating the Effect of MgO/Al2O3 Ratio on Thermal Behaviors and Structures of Blast Furnace Slag with Low Carbon Consumption

Effect of Al2O3/CaO on the melting and mineral transformation of Ningdong coal ash

Effects of Sodium Carbonate and Sodium Chloride Additives on Alkaline Fusion of Coal Fly Ash

Effect of Al2O3 on the Molten Slag Microstructure Information by Molecular Dynamics Simulation and Experimental Analysis

Effects of Na2CO3/Na2SO4 on catalytic gasification reactivity and mineral structure of coal gangue

Separation of alumina and silica from metakaolinite by reduction roasting−alkaline leaching process: Effect of CaSO4 and CaO

Influence of Na2CO3 on the activation degree and microstructure of coal gasification coarse slag

Effect of B2O3 on the Melting Characteristics and Slag-Matte Separation of Nickel Flash Furnace Melting

Effect of Na 2 CO 3 and CaCO 3 on coreduction roasting of blast furnace dust and high-phosphorus oolitic hematite

Effects of CaO, Al2O3 and MgO on Kinetics of Lead-Rich Slag Reduction

Effect of CO2 atmosphere on Ca-containing mineral transformation behaviors during a Ca dominated coal co-firing with a Si/Al dominated coal in oxy-fuel condition

Effect of B2O3 on the Melting Temperature and Viscosity of CaO–SiO2–MgO–Al2O3–TiO2–Cr2O3 Slag

Effect of additives on flow characteristics and sodium capture efficiency of high alkali coal ash slag

Effect of Ca3(PO4)2 additive on the slagging behavior during the cofiring of high‐sodium coal and iron-rich coal

Conversion of barium sulfate into barium carbonate in rare earth acid insoluble slag using low-temperature roasting with sodium hydroxide

Effects of SiO2, CaO and basicity on reduction behaviors and swelling properties of fluxed pellet at different stages