Abstract:Porous ceramic materials usually require an optimal porosity and pore-size distribution to maximize the yield of the required function. In the starch consolidation forming for porous ceramic materials, the porosity and pore size distribution are corresponding closely to the particle size and swelling property of starch. In order to control the porosity and pore size distribution of the porous alumina ceramics, different modified starches with different amounts were added to the alumina slurry with a 58 vol% alumina solid volume loading. The effects of different modified starches and their content on the rheological behavior of the alumina slurry and the porosity, pore size distribution, compressive strength and microstructure of the sintered body were investigated. The results indicated that alumina/starch composite slurry still maintain stable and plastic in suitable condition of slurry preparation. After drying and sintering, materials with ultimate porosities between 22.7 and 68.7% were obtained. The pore of the resulting materials distributed uniformly and the average size was varied from 10 to 40 mu m. It concluded that the average size was controlled by the modified starch type, amount and the degree of modification. When the amount of the modified starches was reached to 60 vol% the porosities of the sintered samples were varied from 63.5 to 68.7% with different modified starch type and their bending strength varied within the range of 24-32 MPa.

Influence Of Slurry Ph On The Compaction Pressing Of Alumina Ceramics

Slurry Dispersion State As a Parameter to Control Internal Structure of Alumina Green Compact

Plastic Deformation and Sintering of Alumina under High Pressure

Influence of Particle Size Distributions with Various Geometrical Standard Deviations on Slip-Cast Forming and Sintering Behavior in Submicron Alumina Powder Compacts

Preparation and Sintering Properties of Alumina Slurries with High Solid Loading

Influence of Alumina Slurry on Morphology of Microspheres by Spray Drying

De-stabilization Mechanism and in Situ Solidification of Alumina Slurry Dispersed in Silica Sol

STUDY ON PREPARATION OF STABLE SLURRIES OF Αalumina POWDERS WITH DIFFERENT PARTICLE SIZES

Formation and Control of Agglomerates in Alumina Powder

Influence of Particle Size and Aggregates on Translucent Alumina Ceramics Fabricated by Gelcasting

Controlling Porosity and Pore Size Distribution of Alumina Ceramics in Consolidation Forming Process Using Modified Starches

PARTICLE-STABILIZED FOAMS SLURRY AND MANUFACTURING OF POROUS ALUMINA CERAMICS

Rheological Behaviours Of Slurries And Mechanical Properties Of Alumina With Additives

Rheological Behavior of Modified Starch-Alumina Oxide Suspensions

The Influence of Rheology for Different Superplasticizer on High Alumina Low Cement Castable

Effect of Dispersants on the Rheological Properties and Slip Casting of Concentrated Alumina Slurry

Effect of Flash Calcined Powders on the Properties of Spherical Alumina Granules

Sintering Shrinkage Anisotropy of Spherical Alumina Powder Compacts with Particle Orientation

Surface Treatment and Modification of Al2O3 Powders

Effect of Cold Isostatic Pressing on Microstructure and Shrinkage Anisotropy During Sintering of Uniaxially Pressed Alumina Compacts

Hydrophobic coagulation of alumina slurries