Abstract:Alumina microspheres were prepared by centrifugal spray drying using alumina powder as a starting material. The influences of solid loading and dispersant addition amount in alumina slurry on the performance of the green body were investigated. The formation mechanism of apple-shaped green body was also discussed. The number of sphere-shaped green body first increases, and then decreases with the increase of solid loading. When the dispersant addition amount increases, the number of sphere-shaped green body first increases and then decreases. An aqueous slurry with 40% (in volume fraction) of alumina and 0.5% (in mass fraction) of dispersant addition amount can be transformed into a green body with microspheres, obtaining a high pellet yield of 92.9%. The solid loading of alumina slurry has a dominant effect on the apple-shaped green body. When solid loading is 20%, the distance between particles is 0.549μm, the proportion of spherical green body is 14.6%, including most apple-shaped green bodies. When solid loading is 40%, the distance between particles is 0.157μm, and the proportion of spherical green body is 92.9%. A lower solid loading results in a greater space, causing the more holes in the green bodies. As a result, massive apple-shaped green bodies appear. The two-step sintering process is adopted to prepare alumina microspheres, and the compressive strength of microspheres sintered at 1700℃ can reach 105.6 MPa.

Influence of Alumina Slurry on Morphology of Microspheres by Spray Drying

Preparation and Sintering Properties of Alumina Slurries with High Solid Loading

Preparation and characterization of Cr 2 AlC microspheres prepared by spray-drying granulation

Study On The Rheological Behavior Of Sub-Micron Alumina Aqueous Suspensions

Influence of Particle Size Distributions with Various Geometrical Standard Deviations on Slip-Cast Forming and Sintering Behavior in Submicron Alumina Powder Compacts

Influence of the Dispersant on the Bead Milling of Alumina

De-stabilization Mechanism and in Situ Solidification of Alumina Slurry Dispersed in Silica Sol

Hydrophobic coagulation of alumina slurries

Spray Freeze Granulation of Submicron Alumina and Its Sintering Behavior Via Spark Plasma Sintering

Fabrication of Alumina Green Body Through Gelcasting Process Using Alginate

DISPERSIBILITY MECHANISM AND SPRAY DRYING OF SiC AQUEOUS SLURRY

Re-fluidising the aged gel for high-density alumina green body

Inter-particle interactions of alumina powders in UV-curable suspensions for DLP stereolithography and its effect on rheology, solid loading, and self-leveling behavior

Effects of glycerol addition on the slurry dispersion and mechanical properties of alumina ceramics prepared by gel-casting process

Model and Experimental Investigations of Aluminum Oxide Slurry Transportation and Vaporization Behavior for Nebulization Inductively Coupled Plasma Optical Emission Spectrometry

Surface Treatment and Modification of Al2O3 Powders

The effect of spray drying parameters on drying of magnesium silicate hydroxide microspheres

Formation and Control of Agglomerates in Alumina Powder

Synthesis and sintering behavior of a nanocrystalline α-alumina powder

Stabilization mechanism of alumina powder dispersed in silica sol

The Influences of Solid Loading and Molding Variables on Alumina Injection Molding