Abstract:Laser-induced damage of fused silica optics at 351 nm is a key factor limiting the output energy of high-power laser facility, especially the damage growth process. A comprehensive understanding of its damage growth behavior is of critical importance for high-power laser facility. Thus we study the laser-induced damage growth on the exit surface of fused silica under the subsequent illumination of 5 ns square pulses at 351 nm on a large-aperture high-power laser facility. Experiment is conducted with a 36 cm thick UV grade fused silica focus lens in clean atmosphere and at room temperature. 56 laser shots of 3 fluence in a range from 0.1 J/cm2 to 8.1 J/cm2 are fired during the experiment. And the damage initiation process and growth process are monitored and recorded with an online optics damage inspection instrument which has an optical resolution of about 50 m. Experimental results demonstrate that the sizes of exit-surface damage sites exponentially or linearly grow with laser shots and the damage growth rate increases with laser fluence. However, it is found that even under the same laser conditions the damage grow rate is not a fixed value, which means that besides the laser fluence other parameters also influence the damage grow process. In order to highlight some tendencies, we consider the single-shot damage growth rate and calculate the average of inside fluence bins. Statistical analysis shows that smaller sites tend to grow with larger growth rates than larger sites under the irradiation of the same laser fluence. This result indicates that damage growth rate is influenced by both laser fluence and damage site size. It suggests that the damage growth rule needs to be incorporated into a size-dependent growth effect. The result that higher growth rates are obtained for small damage sites may be related to the damage growth mechanism of fused silica. Damage crater of fused silica consists of a central core and numerous surrounding cracks. The defects in the central core absorb laser energy and yield plasma, then the plasma pressure will open the cracks on the periphery of the crater and lead to lateral and axial expansion of cracks which can be identified as damage growth. The fact that smaller sites grow faster than larger sites implies that smaller sites more efficiently couple laser energy into fracture energy. Our results have important implications for both the prediction of fused silica optics lifetime and the fundamental understanding of laser damage mechanism.

Damage Morphologies of Al2O3 and Fe Particles Attached on the Input Surface of Fused Silica after Irradiation by a 355 Nm Laser.

Damage Behaviors of Silica Microparticles on Fused Silica Optics under 355 Nm High Fluence Laser

Optical Properties and Laser Damage Performance of Sio2 Irradiated by High-Power Pulsed Electron Beam

Ab Initio Molecular Dynamics Simulation of the Effect of Impurities on Laser-Induced Damage of Fused Silica

Morphology and Growth Properties of Nano- and Submicrometer-Scale Initial Damage Sites under 355 Nm Wavelength Pulsed Laser Irradiation.

Laser-Induced Damage Growth on Larger-Aperture Fused Silica Optical Components at 351 Nm

Atomic Simulation of Surface Damage of Fused Silica under Laser Irradiation

Material migration and damage characteristics of fused silica optical surface treated by CO 2 laser/short – pulse ultraviolet laser

Laser Induced Damage Characteristics of Fused Silica Optics Treated by Wet Chemical Processes

Investigation of the Multimechanism Laser Cleaning Dynamics for Rough Fused Silica Surfaces with Organic Contaminants: A Computational Simulation and Atomic Analysis.

Laser-induced Damage Growth of Fused Silica at 351 Nm on a Large-Aperture High-Power Laser Facility

Laser Damage Induced by Contamination Particles on Coated Optical Components

The Adsorption Behavior Between Particle Contamination And Fused Silica In High-Energy Laser System

Morphology evolution mechanisms and localized structural modification of repaired sites on fused silica optics processed by CO2 laser rapid ablation mitigation

Damage Growth Characteristics of Different Initial Damage Sites of Fused Silica under 355 Nm Small Laser Beam Irradiation

Detailed Near-Surface Nanoscale Damage Precursor Measurement and Characterization of Fused Silica Optics Assisted by Ion Beam Etching

Characterization of laser damage performance of fused silica using photothermal absorption technique

Morphological and Damage Growth Characteristics of Shell-Type Damage of Fused Silica Optics Induced by Ultraviolet Laser Pulses.

Effects of CO2 Laser Irradiation on Surface Morphology and Stress Distribution of Fused Silica

Bulk Damage and Stress Behavior of Fused Silica Irradiated by Nanosecond Laser

Irradiation Effects of CO2laser Parameters on Surface Morphology of Fused Silica