Abstract:This study examines the laser-stricken damage to different alumina ceramic surfaces of different roughness through multi-physical field coupling simulations and laser-striking experiments. The surfaces of different morphologies can be described by waves of different frequencies and amplitudes, and the waves which are discretized can be described by rectangular microstructures of different heights. In this paper, we found that the reaction of roughness surfaces to gauss lasers stricken on them could be simulated by the reaction of rectangular microstructures of different heights to laser strike. The simulation was carried out through the multi-physical field coupling method. The distribution of temperature and stress on rectangular microstructure were examined after being treated by high energy laser. It was found that overhigh temperature and stress were the main causes of laser-stricken damage, but there existed a critical rectangular column height value. The microstructure became increasingly prone to damage and fall-off with the increase of the rectangular column's height, but it became decreasingly prone to damage after the rectangular column reached the critical value. In the experiments, seven roughness zones of alumina ceramic layer were chosen as sample surfaces for laser-striking experiment. The results showed that there was a critical roughness value at a fixed laser energy density. As a result, the amount of particles falling off the surfaces caused by laser strike was rising when the roughness was increasing. However, the amount of particles falling off the surfaces was decreasing after roughness reached the critical value. The critical rectangular column height value in the simulation corresponded to the critical roughness value in the experiment. Therefore, an appropriate selection of roughness is an important factor for obtaining high laser-stricken damage threshold.

Effect of Microstructures on Temperature and Stress Distributions of an Irradiated Alumina Surface.

Study on Laser-Stricken Damage to Alumina Ceramic Layer of Different Surface Roughness

Irradiation effects on microstructure, mechanical properties, and lead-bismuth eutectic corrosion resistance of alumina coating

Total-Ionizing-Dose Effects on Al/SiO2 Bimorph Electrothermal Microscanners

Subsurface hardening of Al irradiated with ultrafast infrared laser

Thermal Stress Field and Microstructure Evolution of Ti-6Al-4V Fabricated by Laser Engineered Net Shaping

Effect of microstructure on thermal field distribution of absorption glass with nanosecond laser-irradiated

Computational Modeling and Experimental Validation of Thermal Stress and Melt Pool Characteristics Using High Power Laser Diode Beam on 7075 Aluminum Alloy

Hydrodynamic Effects on the Surface Morphology Evolution of Aluminum Alloy under Intense Pulsed Ion Beam Irradiation

Experimental and numerical investigation on the ablation mechanism of Al2O3/Al2O3-CMCs under continuous-wave laser irradiation

Investigation of temperature field for the in-situ fabrication of particle-reinforced alumina ceramics coating via laser induction

Atomic Origins of Radiation-Induced Defects and Interfacial Strengthening in Additively Manufactured Titanium Aluminide Alloy Irradiated with Kr-Ions at Elevated Temperature

Experimental and Thermal Stress Field Numerical Simulation Study on Laser Metal Deposition of Ti-48Al-2Cr-2Nb Alloy

Numerical Simulation and Experimental Analysis of Thermal Conduction and Stress in Laser Cladding Repair of Thin-Walled Parts

Surface Treatment of Alumina-Based Ceramics Using Combined Laser Sources

Microwave thermal stress method cutting Al2O3 ceramics: modeling and experiments

Numerical Simulation and Experimental Investigation of Laser Ablation of Al2O3 Ceramic Coating

The influence of thermal distribution on macro profile and dendrites morphology based on temperature field simulation of 6061 aluminum alloy laser welded joint

Study on thermal stress of the the fused silica irradiated by millisecond–nanosecond combined pulse laser

Effects of He Irradiation on Ti3AlC2: Damage Evolution and Behavior of He Bubbles

Microstructure, Morphology and Their Annealing Behaviors of Alumina Films Synthesized by Ion Beam Assisted Deposition