Abstract:Graphite/Cu bonding is essential for the fabrication of graphite-based plasma-facing parts and graphite-type commutators. Transient liquid phase bonding of graphite/Cu has been conducted separately with Ti/Cu/Ti and Ti/Cu/Ni/Ti multi-foils. The interfacial microstructure and mechanical properties of the bonded joints have been characterized. For the joint with Ti/Cu/Ti multi-foils, complete melting of the Ti/Cu/Ti multi-foils and interdiffusion between the molten zone and the Cu substrate occur during the bonding process, leading to formation of Ti–Cu intermetallics in the bonding area. The liquid phase flowing toward the sidewall of the Cu substrate gives rise to a thickness of the bonding area far less than those of the as-received multi-foils. For the joint with Ti/Cu/Ni/Ti multi-foils, the bonding area can be divided into three parts (areas I, II and III). The bonding areas I and III comprise Ti–Cu intermetallics and Ti(Cu x Ni 1-x ) 2 , while the bonding area II consists of an Ni layer and two thin TiNi 3 reaction layers. The thickness of the whole bonding area is similar to those of the as-received multi-foils, indicating that addition of Ni foil can prevent the loss of liquid phase zone by inhibiting the excessive liquid phase formation. The addition of a Ni foil in bonding of the graphite/Cu may alleviate the joint residual stress by its intermediate coefficient of thermal expansion (CTE) to accommodate any thermal mismatch in the joint and by its superior ductility and plasticity, thus resulting in shear strength promotion of the joint with the Ti/Cu/Ni/Ti multi-foils by approximately 35% when compared to the Ti/Cu/Ti multi-foils.

Brazing of graphite to tungsten using graphene nanoplates reinforced TiNiCu composite filler

Microstructure and mechanical properties of C/C composite joint brazed with Ni-based filler

Brazing of C/C Composite and TiAl Alloy Using TiNiSi Filler Metal Added Cu Interlayer

Ultra-high temperature brazing of C/C composite using pure Ni as filler based on eutectic reaction

Microstructural and Mechanical Characterizations of Mo/W and Mo/Graphite Joints with BNi2 Paste

Microstructure and Performance of Graphite/Copper Joints by Brazing with Different Interfacial Structures

Study on the structure and thermal properties of graphite/copper laminated composites assembled by Ti-containing active filler metals

Effect of Ti content on microstructure and mechanical properties of SiCf/SiC composites/GH536 superalloy joints brazed with CoFeCrNiCuTi high entropy filler

Tungsten/steel diffusion bonding using Cu/W–Ni/Ni multi-interlayer

Reactive composite brazing of C/C composite and GH3044 with Ag–Ti mixed powder filler material

Microstructural evolution and mechanical property of a SiCf/SiC composite/Ni-based superalloy joint brazed with an Au-Cu-Ti filler

Mechanical and microstructural characterization of brazing joints of the TiC/Cu–20Ni composite to Cu–20Ni

Enhanced interfacial bonding and mechanical properties of (TiC p +GNPs)/Cu composites by Ti-induced GNPs/Cu interfacial modification

Brazing of C/C composites and 304 stainless steels via Ni/Mo composite interlayer

Microstructure and mechanical properties of Si3N4 ceramic and (TiB + Y2O3)/Ti matrix composite joints brazed with AgCu/Cu foam/AgCu multilayered filler

Vacuum Brazing of C/C Composite and TiAl Intermetallic Alloy Using BNi-2 Brazing Filler Metal

Interfacial Bonding and Strength of Tungsten to Copper or Its Alloy Joints with Ti Foil and Ti/Ni/Ti Multiple Interlayers

Microstructural evolution and mechanical properties of Ni-based superalloy joints brazed using a ternary Ni-W-B amorphous brazing filler metal

AgCuTi/graphene-reinforced Cu Foam: A Novel Filler to Braze ZrB2-SiC Ceramic to Inconel 600 Alloy

Effect of bonding process on the microstructures and strength of W/steel joints with a W-Cu-Ni interlayer

Bonding of graphite to Cu with metal multi-foils