Uncovering the microstructural and precipitate evolution in the cryogenic temperature - Friction stir processed AA6xxx sheets

Aman Gupta,Preetham Alluri,Khushahal Thool,Shi-Hoon Choi
DOI: https://doi.org/10.1016/j.matchar.2024.114619
IF: 4.537
2024-12-08
Materials Characterization
Abstract:In this study, we investigated the microstructural and precipitate evolution in AA6xxx sheets subjected to friction stir processing (FSP) at cryogenic temperature (CT). AA6xxx sheet samples underwent CT-FSP with a tool rotation speed of 800 RPM and a feed rate of 500 mm/min. A homogeneously distributed refined microstructure was observed throughout the FSPed region. The AA6xxx samples contained coarse Al-Fe-Si and Mg 2 Si precipitate particles. Deep learning-based segmentation was utilized to analyze the distributions, and sizes of precipitates in the stir zone (SZ) and the thermo-mechanically affected zone (TMAZ). After the CT-FSPed, dissolution of precipitates and decrease in the equivalent circle diameter (ECD) occurred for both type of particles. The microhardness values of the CT-FSPed samples were lower than those of the initial sample, due to dynamic softening and precipitate dissolution occurring during the process. However, CT-FSPed samples exhibited high formability, as demonstrated by excellent V-bend and hemming results. An interrupted hemming test revealed the reasons for crack initiation in the initial AA6xxx sample. The formation of strain localizations (SLs), the presence of coarse second-phase particles, and a strong (100) texture contributed to crack initiation in the initial sample. In contrast, a strong (101) texture, grain refinement, DRX, and fine precipitates were identified as possible reasons for the improved hemmability of the CT-FSP samples.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing
What problem does this paper attempt to address?