Revealing the Effects of Friction Stir Processing on the Microstructural Evolutions and Mechanical Properties of As‐Cast Interstitial FeMnCoCrN High Entropy Alloy
A. Abbasi,A. Zarei-Hanzaki,J. Charkhchian,A. Moshiri,N. Akhavan,Jongwon Lee,Nokeun Park,H.R. Abedi
DOI: https://doi.org/10.1002/adem.202301908
IF: 3.6
2024-02-23
Advanced Engineering Materials
Abstract:The present study aims to investigate the effect of friction stir processing (FSP) on the microstructural evolutions and mechanical properties of a non‐equiatomic interstitial high entropy alloy (HEA). To achieve this, an as‐cast FeMnCoCrN interstitial HEA undergoes FSP to modify the as‐cast microstructure and investigate the resulting effects on mechanical properties. The grain size, sub‐boundaries, martensite fraction, and accommodated strain exhibited a gradient from the base metal (BM) to the stir zone (SZ). As a result of FSP, the average grain size in the upper SZ (USZ) was significantly decreased from approximately 700 μm in BM to 1.5 μm, which is around 500 times finer than that of the BM. Furthermore, the martensitic transformation in a single metastable FCC phase was specifically occurred in the thermo‐mechanical affected and heat‐affected zones (TMAZ and HAZ). Continuous and geometric dynamic recrystallization (CDRX and GDRX) triggered by FSP led to the development of a refined equiaxed microstructure. This gradient microstructure, in turn, played a pivotal role in achieving significantly improved mechanical properties when compared to the as‐cast microstructure. Remarkably, the yield strength doubled, the ultimate tensile strength increased from 548 MPa to 852 MPa, and ductility increased by 16%. This article is protected by copyright. All rights reserved.
materials science, multidisciplinary