Micro-nano structure characteristics and texture evolution of the friction stir processed dual-phase Mg Li alloy

Luyao Jiang,Wen Jiang,Fei Guo,Weijiu Huang,Haipeng Dong,Hongjun Hu,Qingwei Dai

DOI: https://doi.org/10.1016/j.matchar.2021.110979

IF: 4.537

2021-03-01

Materials Characterization

Abstract:<p>Friction stir processing (FSP) was successfully performed on ultra-light dual-phase LZ91 MgLi alloy, which provided a chance to study the microstructure and texture evolution of this alloy during severe plastic deformation. The results showed that LZ91 MgLi alloy could be processed successfully with 200–400 rpm, 25 mm/min, and water cooling during FSP. No defects were observed on the surface and in the cross-section. The microstructure was strongly influenced by the material flow modes during FSP. Two greatly phase refinement regions were found in the stir zone where the α-Mg and β-Li phases were refined to submicron scale and homogeneously mixed. Maelstrom currents flow between two threads on the pin triggered this phase fragment. The high rotation rate of FSP leads to a remarkable recrystallization and grain growth due to the high heat input. The severe plastic deformation caused a phase transformation inside the refined α-Mg phase. The new phases enriched Li element exhibited a coherent relationship with the matrix. It shows that FSP promoted the short-term diffusion in refined α-Mg.</p>

materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing