Abstract:In this paper, (0.5–5.0 wt%)Gd/316 L composites were prepared by vacuum arc melting, and the microstructure, thermophysical properties, and neutron shielding properties were analyzed deeply. The results showed that the Gd/316 L composites started solidification in primary ferrite mode and terminated solidification by a peritectic-type reaction forming (Fe, Ni, Cr) 3 Gd that is rich in Ni and Gd. In the peritectic-type reaction, local convection in the Ni-rich and Gd-rich peritectic liquid phase leads to the formation of multiple variants of (Fe, Ni, Cr) 3 Gd. The higher the Gd content, the greater the amount of (Fe, Ni, Cr) 3 Gd and ferrite, and the harder it is to keep the austenitic matrix of 316 L stainless steel. The solidification temperature range of Gd/316 L composites is 1074–1460 °C, which severely limits the ability to further process it by high-temperature deformation techniques such as hot rolling or hot forging. (Fe, Ni, Cr) 3 Gd preferentially nucleates and grows in the triangular region of austenite grain boundaries at 1074 °C. At 50–500 °C, with increasing Gd content, thermal expansion and thermal diffusion coefficients become decrease, and thermal conductivity and specific heat capacity increase. The trend of thermophysical property changes is favorable for SNF transportation and storage applications. The thermal neutron shielding properties of 1.0 wt%Gd/316 L composite is comparable to that of 4.45 wt% B content boron steel and 15 wt%B 4 C/Al composite. The Gd content in Gd/316 L composites material should not exceed 2.5 wt%. If the Gd content continues to increase, it is of little significance to improving shielding properties and material thinning. A shielding thickness of 3 mm is more appropriate for Gd/316 L composites. Too thin would not provide sufficient mechanical properties and increase processing and manufacturing costs.

Early-stage Corrosion Behavior of Al-based Gd2O3–W Shielding Composites in a Simulated Spent Fuel Wet Storage Environment

High-temperature corrosion behavior of hot-pressed Al-based Gd2O3-W shielding materials used in spent fuel storage

Ball-milling properties and sintering behavior of Al-based Gd<sub>2</sub>O<sub>3</sub>-W shielding materials used in spent-fuel storage

Corrosion behavior and failure mechanism of amorphous Al2O3 coating at high-temperature LBE

Evolution and characteristics of defect clusters in H2+ irradiated Al-based Gd2O3–W composites used as spent fuel shielding materials

Microstructure and its effect on mechanical and thermal properties of Al-based Gd2O3 MMCs used as shielding materials in spent fuel storage

Corrosion behavior of neutron absorbing Ti-Gd alloys in simulated spent nuclear fuel pool water

Corrosion Behavior of NITE-SiC with Different Sintering Additives at Simulated PWRs Conditions

The Corrosion Behavior of Al/Al2O3 Composite Films with Ultra-Dense Structure Exposed to Lead-Bismuth Eutectic at 450 to 650 °C

Early corrosion behaviour of irradiated FeCrAl alloy in a simulated pressurized water reactor environment

Design and mechanical properties of SiC reinforced Gd2O3/6061Al neutron shielding composites

Corrosion of Zircaloy-4, Zr-1Nb and FeCrAl Alloys in Deaerated Water at 330 °C and 14 MPa: Superior Corrosion Resistance and Corrosion Mechanism of FeCrAl Alloy by Experiments and Molecular Dynamics Simulations

Microstructure, thermophysical properties and neutron shielding properties of Gd/316 L composites for spent nuclear fuel transportation and storage

CORROSION BEHAVIOR OF NUCLEAR GRADE ALLOYS 690 AND 800 IN SIMULATED HIGH TEMPERATURE AND HIGH PRESSURE PRIMARY WATER OF PRESSURIZED WATER REACTOR

Corrosion Onset Associated with the Reinforcement and Secondary Phases in B4C-6061Al Neutron Absorber Material in H3BO3 Solution

Hydrothermal Corrosion Behavior of SiCf/SiC Composites Candidate for PWR Accident Tolerant Fuel Cladding

Corrosion Behavior of High-Level Waste Container Materials Ti and Ti–Pd Alloy under Long-Term Gamma Irradiation in Beishan Groundwater*

A comprehensive XPS investigation of the effect of aqueous corrosion on the surface of glass-zirconolite composite material (Fe–Al–BG–CaZrTi2O7)

Incipient Corrosion of FeCrAl Alloys in H3BO3- and LiOH-containing Pure Water at 360 °C and 18.5 MPa

Design and Preparation of WBX/Al Composites for Nuclear Radiation Protection

Corrosion behavior of additively manufactured FeCrAl in out-of-pile light water reactor environments