Abstract:Creep-fatigue interaction is identified as a primary failure mode for components operating under high temperatures. As operational durations extend, this interaction not only alters the material's microstructures but also initiates a gradual degradation in mechanical properties, significantly impacting its deformation and damage behaviors. In this work, the dynamic microstructural evolution of GH4169 superalloy during creep-fatigue was elucidated via qualitative characterization, and damage level evaluation method was subsequently developed by bridging microstructure degradation to mechanical property degradation. Creep-fatigue tests were performed at 650 °C with various tensile holding times and were interrupted at lifetime fractions of 10 %, 50 % and 80 % for further analysis and tensile evaluations. Results revealed that the prolonged exposure to holding times induced the coarsening of γ″ precipitates alongside an increase in low-angle grain boundaries, culminating a reduction in creep-fatigue strength. The development of voids and cracks exacerbated the degradation of elongation, leading to a hybrid fracture mode encompassing both intergranular and transgranular cracking paths. Synthesizing microstructural evolutions to qualitatively categorize diverse degradation levels imparted a robust physical basis for damage evaluation. A mapping model was established to correlate the average kernel average misorientation (micro-degradation indicator) with the tensile plastic strain energy density (macro-degradation indicator). The damage level evaluation method was endowed with quantitative metrics utilizing this model, and its generality was additionally validated in P92 steel. This work offers an insight into the quantitative damage evaluations of creep-fatigue-induced degradations in materials, thereby providing a theoretical basis for the development of operation management and inspection plans of components.

Time-related creep fatigue damage evaluation method

A New Approach to Low-Cycle Fatigue Damage Based on Exhaustion of Static Toughness and Dissipation of Cyclic Plastic Strain Energy During Fatigue

An online monitoring method for creep-fatigue life consumption with real-time damage accumulation

Evaluation of fatigue and creep-fatigue damage levels on the basis of engineering damage mechanics approach

A New Approach for Studying Fatigue Damage

Assessment of prior fatigue damage and a new approach to predict remanent creep rupture of P92 steel

Research on Fatigue-Creep Interaction Damage of Steel 1.25Cr0.5mo

Oxidation-involved life prediction and damage assessment under generalized creep-fatigue loading conditions based on engineering damage mechanics

A Robust Life Prediction Model for a Range of Materials under Creep-Fatigue Interaction Loading Conditions

ABAQUS-BASED MULTIAXIAL CREEP FATIGUE PREDICTION METHOD

A Modified Microstructure-Based Creep Damage Model for Considering Prior Low Cycle Fatigue Damage Effects

Creep-fatigue Damage Level Evaluation Based on the Relationship Between Microstructural Evolution and Mechanical Property Degradation

Numerical Method for Creep Analysis of Strengthened Fatigue-Damaged Concrete Beams

A creep damage model for low cycle fatigue based on the equivalent creep stress: Establishment, verification and application

Evaluation of the Effect of Various Prior Creep-Fatigue Interaction Damages on Subsequent Tensile and Creep Properties of 9%cr Steel

A Novel Creep-Fatigue Life Evaluation Method for Ceramic-Composites Components

Study on Creep-Fatigue Damage Evaluation for Advanced 9%-12% Chromium Steels under Stress Controlled Cycling

Microstructural Damage Mechanics-Based Model for Creep Fracture of 9%cr Steel under Prior Fatigue Loading

An Efficient Fatigue and Creep‐fatigue Life Prediction Method by Using the Hysteresis Energy Density Rate Concept

A New 3D Creep-Fatigue-Elasticity Damage Interaction Diagram Based on the Total Tensile Strain Energy Density Model

A new creep damage assessment method for metallic material under variable load conditions at elevated temperature