Abstract:Creep-fatigue interaction is identified as a primary failure mode for components operating under high temperatures. As operational durations extend, this interaction not only alters the material's microstructures but also initiates a gradual degradation in mechanical properties, significantly impacting its deformation and damage behaviors. In this work, the dynamic microstructural evolution of GH4169 superalloy during creep-fatigue was elucidated via qualitative characterization, and damage level evaluation method was subsequently developed by bridging microstructure degradation to mechanical property degradation. Creep-fatigue tests were performed at 650 °C with various tensile holding times and were interrupted at lifetime fractions of 10 %, 50 % and 80 % for further analysis and tensile evaluations. Results revealed that the prolonged exposure to holding times induced the coarsening of γ″ precipitates alongside an increase in low-angle grain boundaries, culminating a reduction in creep-fatigue strength. The development of voids and cracks exacerbated the degradation of elongation, leading to a hybrid fracture mode encompassing both intergranular and transgranular cracking paths. Synthesizing microstructural evolutions to qualitatively categorize diverse degradation levels imparted a robust physical basis for damage evaluation. A mapping model was established to correlate the average kernel average misorientation (micro-degradation indicator) with the tensile plastic strain energy density (macro-degradation indicator). The damage level evaluation method was endowed with quantitative metrics utilizing this model, and its generality was additionally validated in P92 steel. This work offers an insight into the quantitative damage evaluations of creep-fatigue-induced degradations in materials, thereby providing a theoretical basis for the development of operation management and inspection plans of components.

Creep-fatigue Damage Level Evaluation Based on the Relationship Between Microstructural Evolution and Mechanical Property Degradation

An Investigation of the Effect of High-Temperature Cyclic Straining and Creep Loading on Tensile Mechanical Properties of GH4145/SQ Alloy

Evaluation of fatigue and creep-fatigue damage levels on the basis of engineering damage mechanics approach

Evaluation of the Effect of Various Prior Creep-Fatigue Interaction Damages on Subsequent Tensile and Creep Properties of 9%cr Steel

Determination of relationship between high-temperature low cycle fatigue damage and mechanical property degradation: Experimental and theoretical analyses

Assessment of prior fatigue damage and a new approach to predict remanent creep rupture of P92 steel

Microstructural Damage Mechanics-Based Model for Creep Fracture of 9%cr Steel under Prior Fatigue Loading

Research on Fatigue-Creep Interaction Damage of Steel 1.25Cr0.5mo

Life prediction and damage analysis of creep-fatigue combined with high-low cycle loading by using a crystal plasticity-based approach

An Insight into the Creep-Fatigue Damage Localization in Welded Joints Based on Crystal Plasticity Finite Element Method

Creep-fatigue life prediction in nickel-based superalloy GH4169 based on microstructural damage quantification with the help of electron backscatter diffraction

Low-Cycle Fatigue-Creep Interaction Behavior of GH4169 Supperalloy

The correlation between prior fatigue damage and remaining creep properties in a high chromium steel welded joint

Semi-quantitative creep-fatigue damage analysis based on diffraction-based misorientation mapping and the correlation to macroscopic damage evolutions

High Temperature Fatigue and Creep-Fatigue Behaviors in a Ni-based Superalloy: Damage Mechanisms and Life Assessment

Creep-fatigue Life Prediction under Fully-Reversed Multiaxial Loading at High Temperatures

Creep-fatigue Life Prediction and Interaction Diagram in Nickel-Based GH4169 Superalloy at 650 °C Based on Cycle-by-cycle Concept

Damage behaviour in different micro-regions of P92 steel weldment under sequential low cycle fatigue and creep loading

A new creep damage assessment method for metallic material under variable load conditions at elevated temperature

Study on Creep-Fatigue Damage Evaluation for Advanced 9%-12% Chromium Steels under Stress Controlled Cycling

Creep-Fatigue Crack Initiation Simulation of a Modified 12% Cr Steel Based on Grain Boundary Cavitation and Plastic Slip Accumulation