The Role of Yb Content on the Microstructural Evolution and Mechanical Characteristics of Cast Mg-9Gd-0.5Zn-0.2Zr Alloy

He Xie,Guohua Wu,Xiaolong Zhang,Jinshuo Zhang,Wenjiang Ding

DOI: https://doi.org/10.1016/j.msea.2021.141292

2021-01-01

Abstract:Inspections on microstructural design suggest that a high-strength Mg alloy can be achieved via the generation of co-precipitation of prismatic and basal precipitates with high number density and large aspect ratios. Currently, there is a lack of feasible approaches to generating such a microstructure. This work investigated the specific role of various Yb contents on the precipitation behavior, solute segregation and mechanical performance of cast Mg-9Gd-xYb-0.5Zn-0.2Zr alloys (x = 0, 0.5, 1 wt%). It was found that, the age hardening response of Mg-9Gd-0.5Zn-0.2Zr alloy could be significantly improved as the Yb addition increased, primarily ascribed to introduction of dense distribution of both prismatic and basal matrix precipitates involving gamma '', beta' and beta(1). Solute segregation of Yb had been examined utilizing high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM), revealing the evidence of strong Yb segregation in both prismatic beta', beta(1) and basal gamma '' precipitates. Quantitative TEM analysis indicated that the increasing Yb addition was found to improve the number density of gamma '', beta' and beta(1) during isothermal ageing at 225 degrees C. The substantial improvement on yield strength (similar to 84 MPa) in peak-aged alloy was thereby achieved due to the co-precipitation of dense prismatic and basal strengthening phases associated with Yb addition (1 wt%). However, in addition to the promoted precipitation of these strengthening phases, Zn-Zr particles were confirmed to act as favorable nucleation sites for prismatic beta(1) phases in the under-aged condition. During prolonged ageing time, the addition of 1 wt% Yb was found to greatly accelerate the growth of these preferentially formed beta(1) phases and part of beta(1) transformed in situ into beta phases, accompanied by the gradual developments of matrix precipitate-free zones (PFZs). The greatly improved uneven distribution of these coarse beta-type phases concomitant with widened PFZs primarily led to the significant reduction in ductility as the Yb content increased up to 1%.