Glass Transition of the Surface Monolayer of Polystyrene Films: Effect of Thermal Preannealing

Jinsong Yan,Zongyi Ma,Jianquan Xu,Haoran Nie,Hailin Yuan,Xinping Wang,Tong Wang,Lu-Tao Weng,Ophelia K. C. Tsui

DOI: https://doi.org/10.1021/acs.macromol.3c00966

IF: 5.5

2023-07-27

Macromolecules

Abstract:In a previous experiment, we observed that the glass transition temperature of the surface monolayer glass transition temperature (T g surf) of unannealed polystyrene (PS) films spin-coated on oxide-coated silicon decreased with decreasing film thickness (h < ∼60 nm). However, this h dependence could be removed by thermal preannealing. In this experiment, we investigated the origin of this preannealing effect. We found that T g surf of the thin films increased with preannealing time (t ANN) and reached the steady-state thick-film value at a characteristic time (τsurf) following the τsurf ∼ h 2 scaling for diffusion. Moreover, chain adsorption occurred alongside the increase in T g surf during thermal preannealing and reached the steady-state adsorbed amount at a time similar to τsurf. We tentatively suggest that the observed increase in T g surf with t ANN was caused by diffusion of free-volume holes from the polymer–substrate interface to the free surface due to densification of the interfacial polymer upon chain adsorption.

polymer science