Hui Zhang,Tongxin Chang,Shuangshuang Zhang,Kun Zhou,Wei Zhang,Zhijun Hu

DOI: https://doi.org/10.1016/j.polymer.2022.124986

IF: 4.6

2022-06-22

Polymer

Abstract:There are substantial debates on the origin of glassy dynamic changes of nanoconfined polymers. We measure the glass transition temperature (Tg) of linear and cyclic polystyrene thin films, and find that the Tg of cyclic polystyrene nearly remains constant when the film thickness is decreased. The Tg of analogous linear polystyrene, however, substantially decreases with decreasing film thickness. When the thin films are patterned into line gratings with a height of about 69 nm, Tg-reduction is observed in both linear and cyclic polystyrene. The magnitude of Tg-reduction of cyclic polystyrene is about 7 K regardless the molecular weight, whereas the Tg-reduction of linear polystyrene ranges from about 20 K to 6 K depending on the molecular weight. These experimental results indicate that the effect of chain ends alone cannot explain the mechanism of confinement-induced Tg depression, and the decreased chain density at interfaces may play an overwhelm role.

polymer science