Thickness Dependence of Glass Transitions Measured by AC-Chip Calorimetry in Films with Controlled Interface

Jiao Chen,Jie Xu,Xiaoliang Wang,Dongshan Zhou,Pingchuan Sun,Gi Xue

DOI: https://doi.org/10.1021/ma401257y

IF: 5.5

2013-01-01

Macromolecules

Abstract:When most prior studies on thin polymer films have shown that glass transition temperature (T-g) decreases under nanoconfinement, the differential alternating current chip (ac-chip) calorimetric method shows little dependence of T-g on thickness for supported film. To reveal this contradiction, we have manipulated a controlled interface by spin-coating polystyrene (PS) with immiscible surfactants such as tetraoctylammonium bromide or citric acid. Since the immiscible surfactants did not show plasticizing effect for PS, there was no observable reduction of T-g from the bulk value ether in powdered blends or in thick films. However, the ultrathin film with thickness h similar to 25 nm, consisting of 95 wt % PS and 5 wt % surfactants, showed a reduction of T-g by 6-7 degrees C, as compared to thick film with the same composition. We propose that the surfactant molecules assembled on the interface between thin film and substrate due to phase separation. The molecular mobility of molecules at the interface was dramatically increased, which was detected by (NMR)-N-1 with dipolar filter sequence. It appeared that the deviation range was not so large as that measured by other methods. But considering that we were measuring T-g at a high frequence (10 Hz), this amount of deviation was quite significant for ac-chip calorimetry. As a result, ac-chip calorimetry measured T-g data unambiguously demonstrate that thickness dependence of T-g is a real property of confined thin film.