Abstract:Nano-ZSM-5 with large amount and high strength of acid sites were successfully synthesized by hydrothermal crystallization of pure-silica nucleus in NaAlO2 alkali solution. The concentration of NaAlO2 alkali solution was decreased by increasing the H2O/Al ratio from 200 to 2600, which strongly determined the acidic properties and crystal size of the obtained nano-ZSM-5. Low concentration of NaAlO2 alkali solution was found unfavorable for the incorporation of Al into the bulk of ZSM-5 crystal in crystallization process. Hence, more Al distributed at the exterior of crystals, which enhanced the accessibility of the acid sites during reaction. Large amount and high strength of acid sites were produced for nano-ZSM-5 by increasing H2O/Al ratio. When the H2O/Al ratio increased from 200 to 2600, the total amount of acid sites increased from 0.59 to 0.81 mmol g(-1), much higher than conventional value of 0.50 mmol g(-1). In addition, the acid strength increased and the ratio of Bronsted/Lewis acid sites were sharply increased from 2.3 to 4.1 when the H2O/Al ratio increased. Moreover, the size of nano-crystal was also decreased by above decreasing the concentration of the NaAlO2 alkali solution. When the H2O/Al ratio was 2600, the obtained sample possessed total acid amount of 0.81 mmol g(-1) and crystal size of 60 nm, respectively. Methanol to hydrocarbon (MTH) reaction results showed that the increased acid sites of the catalyst decreased its catalytic lifetime to some extent, but the aromatics selectivity was tunable obviously. As for the catalyst prepared with H2O/Al ratio of 2000, the aromatics selectivity of the obtained catalyst reached to 66.0%. This paper provided a method for the fabrication of small-size nano-ZSM-5 with large amount and high strength of acid sites and regulated Al distribution for MTH reaction.

Catalytic Synergy Between the Low Si/Al Ratio Zn/ZSM-5 and High Si/Al Ratio HZSM-5 for High-Performance Methanol Conversion to Aromatics

Efficient Conversion of Methane to Aromatics in the Presence of Methanol at Low Temperature

Utilization of Metal-Functionalized ZSM-5 for Methanol and Low-Carbon Hydrocarbon Coupling Aromatization

Relay and Feedback Conversion Effect of Hydrocarbons between ZSM-5 Grains on Product Selectivity and Coke Formation during Methanol Aromatization

Simultaneously enhanced aromatics selectivity and catalyst lifetime in methanol aromatization over [Zn, Al]-ZSM-5 via isomorphous substitution with optimized acidic properties and pore structure

Co-conversion of Methanol and N -Hexane into Aromatics Using Intergrown ZSM-5/ZSM-11 As a Catalyst

Influence of Catalyst Acidity on Dealkylation, Isomerization and Alkylation in Mta Process

Aromatization of Methanol over La/Zn/HZSM-5 Catalysts

Influence of Acid-Base Properties of ZnMgAl-mixed Oxides for the Synthesis of 1-Methoxy-2-propanol

Regulating Hierarchical Structure and Acidity of HZSM-5 for Methanol to Aromatics Via Protective Desiliconization and External Surface Modification

Isomorphous Substitution in ZSM-5 in Tandem Methanol/Zeolite Catalysts for the Hydrogenation of CO 2 to Aromatics

Effect of the Si/Al Ratios of Nanocrystalline HZSM-5 Zeolite on the Performance in Catalytic Conversion of Ethanol to Propylene

Controllable Synthesis of Nano-Zsm-5 Catalysts with Large Amount and High Strength of Acid Sites for Conversion of Methanol to Hydrocarbons

Synthesis of Aromatics from Syngas over FeMnK/SiO2 and HZSM-5 Tandem Catalysts

Two-way Desorption Coupling to Enhance Syngas to Aromatics by MnO/H-ZSM-5

A Multi-Stage Fluidized Bed Strategy for the Enhanced Conversion of Methanol into Aromatics

Direct Transformation of Syngas to Aromatics over Na-Zn-Fe5C2 and Hierarchical HZSM-5 Tandem Catalysts

Products distribution in methanol to gasoline over HZSM-5 Catalysts with different Si/Al ratio

Boosting Methanol-Mediated CO2 Hydrogenation into Aromatics by Synergistically Tailoring Oxygen Vacancy and Acid Site Properties of Multifunctional Catalyst

Si/Al Ratio Induced Structure Evolution During Desilication-Recrystallization of Silicalite-1 to Synthesize Nano-Zsm-5 Catalyst for MTH Reaction

Aromatization of Methanol on Ag/ZSM-5 Catalyst