The plastic crystal composite polyacrylate polymer electrolyte with a semi-interpenetrating network structure for all-solid-state LIBs

Kewu He,Lei Zhao,Zhenbo Wang,shujian Zhang,yang Lu,lanfang Que

DOI: https://doi.org/10.1039/d2nj04022k

IF: 3.3

2022-10-18

New Journal of Chemistry

Abstract:In order to overcome the tradeoff between mechanical and electrochemical properties of polymer electrolytes, a novel semi-interpenetrating network structure is proposed. It can effectively solve the problems of low conductivity, poor interface stability, and weak mechanical strength of polymer electrolytes. Specifically, we use a plastic crystal composite polyacrylate polymer electrolyte doped with PVDF-HFP, after in-situ UV curing, the polymer matrix with a semi-interpenetrating structure is formed by linear PVDF-HFP and cross-linked polyacrylate network structure (S-PCCE). A significant feature of the semi-interpenetrating network structure is the fine integration of the cross-linked polymer network and the linear polymer, resulting in synergistic effects that can improve the flexibility, mechanical strength, and ionic conductivity of the plastic-crystal composite polymer electrolyte. The ionic conductivity can reach 1.45×10-3 S/cm at room temperature and 4.8×10-3 S/cm at 60°C, which is conducive to high battery performance. The LiFePO4/S-PCCE/Li battery has an initial discharge specific capacity of 156 mAh/g and a maximum discharge specific capacity of 163 mAh/g at 0.2C. After 50 cycles, the battery can still maintain a high discharge specific capacity of 155 mAh/g and a Coulomb efficiency of 99.4%. At the same time, the thermogravimetric curve shows that the electrolyte has good adaptability to high temperatures. Therefore, polymer electrolytes with a semi-interpenetrating network structure have a good application prospect.

chemistry, multidisciplinary