CuO@CoFe Layered Double Hydroxide Core–Shell Heterostructure as an Efficient Water Oxidation Electrocatalyst under Mild Alkaline Conditions
Yuting Wang,Ting Wang,Rong Zhang,Qian Liu,Yongsong Luo,Guanwei Cui,Siyu Lu,Jiahai Wang,Yongjun Ma,Xuping Sun
DOI: https://doi.org/10.1021/acs.inorgchem.0c01927
IF: 4.6
2020-07-07
Inorganic Chemistry
Abstract:Designing hierarchical electrocatalysts with superior water oxidation performance is highly desirable for the production of renewable chemical fuels. Here, we report the development of a layered double hydroxide core–shell heterostructure supported on Cu foil (/CF) as a highly active catalyst electrode for water oxidation under mild alkaline conditions. In a 0.2 M carbonate buffer solution (pH 11), it only needs a small overpotential of 213 mV to achieve 10 mA cm<sup>–2</sup>, outperforming all reported electrocatalysts at comparable testing conditions. It also shows outstanding long-term durability.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.inorgchem.0c01927?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.inorgchem.0c01927</a>.Experimental section, EDX elemental mapping images, CV and LSV curves, XRD pattern, XPS spectra, SEM and TEM images, Nyquist plots, and Tables S1 and S2 (<a class="ext-link" href="/doi/suppl/10.1021/acs.inorgchem.0c01927/suppl_file/ic0c01927_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, inorganic & nuclear